Stress-relief cracking mechanism in simulated coarse-grained heat-affected zone of T23 steel | |
Li, Yong; Wang, Xue; Wang, Jiaqing; Chen, Ansheng | |
刊名 | JOURNAL OF MATERIALS PROCESSING TECHNOLOGY |
2019 | |
卷号 | 266 |
关键词 | T23 steel Stress-relief cracking Precipitates Depletion of alloy element |
ISSN号 | 0924-0136 |
DOI | 10.1016/j.jmatprotec.2018.10.028 |
URL标识 | 查看原文 |
收录类别 | EI ; SCIE |
语种 | 英语 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/4215610 |
专题 | 武汉大学 |
推荐引用方式 GB/T 7714 | Li, Yong,Wang, Xue,Wang, Jiaqing,et al. Stress-relief cracking mechanism in simulated coarse-grained heat-affected zone of T23 steel[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,2019,266. |
APA | Li, Yong,Wang, Xue,Wang, Jiaqing,&Chen, Ansheng.(2019).Stress-relief cracking mechanism in simulated coarse-grained heat-affected zone of T23 steel.JOURNAL OF MATERIALS PROCESSING TECHNOLOGY,266. |
MLA | Li, Yong,et al."Stress-relief cracking mechanism in simulated coarse-grained heat-affected zone of T23 steel".JOURNAL OF MATERIALS PROCESSING TECHNOLOGY 266(2019). |