The effect of Li-substitution on the M-phases of AgNbO3 | |
Khan, H. U.1; Sterianou, I.1; Miao, S.1,2; Pokorny, J.1,3; Reaney, I. M.1 | |
刊名 | journal of applied physics |
2012-01-15 | |
卷号 | 111期号:2 |
英文摘要 | ceramics in the solid solution, lixag1-xnbo3 (lan) with 0 <= x <= 0.20, have been synthesized by the mixed oxide method. x-ray diffraction (xrd) revealed that only compositions with x <= 0.05 were single phase which were indexed according to pbcm symmetry with a unit cell, root 2a(p) x root 2a(p) x 4a(p) (where a(p) is the fundamental perovskite lattice parameter). for compositions with x >= 0.1, second phase peaks attributed to linbo3 were observed and the matrix phase transformed to a metrically rhombohedral structure according to xrd. a phase transition at 0.05 < x <= 0.1 was confirmed by raman spectroscopy and electron diffraction but the latter technique revealed superstructure reflections for x >= 0.1 at +/- 1/6{00l} and 1/2{ooo} +/- 1/6{00l} (where o = odd). these support the premise that li doping invokes a new complex modulated tilt system with a root 2a(p) x root 2a(p) x 6a(p) unit cell rather than root 2a(p) x root 2a(p) x 4a(p) (pbcm). reflections of the type +/- 1/6{00l} are, however, streaked along the inverted right perpendicular001inverted left perpendicular direction indicating that the structure may be incommensurate or only partially ordered. the appearance of the root 2a(p) x root 2a(p) x 6a(p) structure is associated with strong asymmetry in the peak in permittivity attributed to the m-3-m-2 and a decrease in intensity of the peak in permittivity associated with the m-2-m-1 transition. slim polarization versus field curves characteristic of weak ferroelectricity were observed for compositions with x <= 0.05 but for higher values of x the loops were unsaturated albeit with larger remanent polarization. (c) 2012 american institute of physics. [doi: 10.1063/1.3677871] |
WOS标题词 | science & technology ; physical sciences |
类目[WOS] | physics, applied |
研究领域[WOS] | physics |
关键词[WOS] | agnb1-xtaxo3 solid-solutions ; niobate single-crystals ; dielectric-properties ; silver niobate ; piezoelectric properties ; ferroelectric phase ; raman-scattering ; lithium-niobate ; transitions ; ceramics |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000299792400065 |
公开日期 | 2015-11-17 |
内容类型 | 期刊论文 |
源URL | [http://159.226.238.44/handle/321008/142956] |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | 1.Univ Sheffield, Dept Mat Sci & Engn, Sheffield S1 3JD, S Yorkshire, England 2.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Peoples R China 3.Acad Sci Czech Republic, Inst Phys, Prague 18221 8, Czech Republic |
推荐引用方式 GB/T 7714 | Khan, H. U.,Sterianou, I.,Miao, S.,et al. The effect of Li-substitution on the M-phases of AgNbO3[J]. journal of applied physics,2012,111(2). |
APA | Khan, H. U.,Sterianou, I.,Miao, S.,Pokorny, J.,&Reaney, I. M..(2012).The effect of Li-substitution on the M-phases of AgNbO3.journal of applied physics,111(2). |
MLA | Khan, H. U.,et al."The effect of Li-substitution on the M-phases of AgNbO3".journal of applied physics 111.2(2012). |