Properties of Polymer Electrolyte Membranes Based on Poly(Aryl Ether Benzimidazole) and Sulphonated Poly(Aryl Ether Benzimidazole) for High Temperature PEMFCs | |
Dai, H.1,2; Zhang, H.1; Zhong, H.1; Jin, H.1,2; Li, X.1; Xiao, S.1,2; Mai, Z.1,2 | |
刊名 | fuel cells |
2010-10-01 | |
卷号 | 10期号:5页码:754-761 |
关键词 | Fuel Cell Performance High Temperature PEMFCs OPBI Properties SOPBI |
英文摘要 | membranes based on poly[2,2'-(p-oxydiphenylene)-5,5'-bibenzimidazole] (opbi) and their sulphonated derivatives (sopbi) were prepared and first investigated for high temperature proton exchange membrane fuel cells. opbi and sopbi membranes with good chemical stability were prepared by casting from their dimethyl sulphoxide ( dmso) solution and then impregnated in phosphoric acid baths to obtain h(3)po(4) (pa)-doped membranes. the properties of pa-doped opbi membranes, including phosphoric acid uptake, swelling ratio, mechanical properties and thermal properties, were fully investigated and compared with pa-doped sopbi membranes. the fuel cell performances of pa-doped opbi and sopbi membranes at different temperatures were first evaluated. when doped in different concentrations of h(3)po(4) solution, opbi membranes adsorb more acid than sopbi membranes. sopbi membranes exhibit obviously lower swelling ratio in thickness direction than that of opbi membranes. with an acid uptake of similar to 110 wt.%, corresponding doping level around 5, pa-doped opbi and sopbi membranes keep reasonably high tensile strength. pa-doped opbi membranes exhibit peak power density of 0.78 w cm(-2) at 170 degrees c and 0.25 mpa. with the same acid uptake, pa-doped sopbi membranes displayed similar fuel cell performance to that of pa-doped opbi membranes. |
WOS标题词 | science & technology ; physical sciences ; technology |
类目[WOS] | electrochemistry ; energy & fuels |
研究领域[WOS] | electrochemistry ; energy & fuels |
关键词[WOS] | acid doped polybenzimidazole ; fuel-cell application ; phosphoric-acid ; pbi ; conduction |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000284057800003 |
公开日期 | 2015-11-17 |
内容类型 | 期刊论文 |
源URL | [http://159.226.238.44/handle/321008/141887] |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Lab PEMFC Key Mat & Technol, Dalian 116023, Liaoning, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Dai, H.,Zhang, H.,Zhong, H.,et al. Properties of Polymer Electrolyte Membranes Based on Poly(Aryl Ether Benzimidazole) and Sulphonated Poly(Aryl Ether Benzimidazole) for High Temperature PEMFCs[J]. fuel cells,2010,10(5):754-761. |
APA | Dai, H..,Zhang, H..,Zhong, H..,Jin, H..,Li, X..,...&Mai, Z..(2010).Properties of Polymer Electrolyte Membranes Based on Poly(Aryl Ether Benzimidazole) and Sulphonated Poly(Aryl Ether Benzimidazole) for High Temperature PEMFCs.fuel cells,10(5),754-761. |
MLA | Dai, H.,et al."Properties of Polymer Electrolyte Membranes Based on Poly(Aryl Ether Benzimidazole) and Sulphonated Poly(Aryl Ether Benzimidazole) for High Temperature PEMFCs".fuel cells 10.5(2010):754-761. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论