Oxygen permeability and structural stability of BaCe0.15Fe0.85O3-delta membranes | |
Zhu, Xuefeng; Cong, You; Yang, Weishen | |
刊名 | journal of membrane science
![]() |
2006-10-20 | |
卷号 | 283期号:1-2页码:38-44 |
关键词 | oxygen separation ceramic membrane perovskite mixed conductor structural stability |
英文摘要 | cobalt-free bacexfe1-xo3-delta (x = 0.15-0.85) membranes have both high oxygen permeation flux and high structure stability even in reducing atmosphere at high temperature. the oxygen flux of bace0.15fe0.85o3-delta (bcf1585) membrane reached at 0.5 ml/min cm(2) at 900 degrees c with a thickness of 1.4 mm. oxygen permeation results showed that oxygen permeation controlling step mainly was oxygen ion diffusion in the membrane bulk if the membrane thicker than 1.0 mm, and mainly was surface oxygen exchange if the membrane thinner than 0.78 mm. ba0.5sr0.5co0.8fe0.2o3-delta (bscf) porous layer coated on the membrane surfaces could effectively accelerate the surface oxygen exchange rate, thus greatly improve the oxygen permeability of the membrane. in some cases, the oxygen permeation flux of the membrane coated with bscf was even two times higher than that of the membrane without coating. perovskite structure of bcf1585 was still maintained at 950 degrees c even after it was exposed to 5% h-2 + ar mixture gas for 1 h. (c) 2006 elsevier b.v. all rights reserved. |
WOS标题词 | science & technology ; technology ; physical sciences |
类目[WOS] | engineering, chemical ; polymer science |
研究领域[WOS] | engineering ; polymer science |
关键词[WOS] | perovskite-type oxides ; dense ceramic membranes ; partial oxidation ; methane conversion ; ionic-conductivity ; permeation ; syngas ; reactor ; fe ; performance |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000240844900007 |
公开日期 | 2015-11-17 |
内容类型 | 期刊论文 |
源URL | [http://159.226.238.44/handle/321008/140347] ![]() |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China 2.Chinese Acad Sci, Grad Sch, Dalian 116023, Peoples R China |
推荐引用方式 GB/T 7714 | Zhu, Xuefeng,Cong, You,Yang, Weishen. Oxygen permeability and structural stability of BaCe0.15Fe0.85O3-delta membranes[J]. journal of membrane science,2006,283(1-2):38-44. |
APA | Zhu, Xuefeng,Cong, You,&Yang, Weishen.(2006).Oxygen permeability and structural stability of BaCe0.15Fe0.85O3-delta membranes.journal of membrane science,283(1-2),38-44. |
MLA | Zhu, Xuefeng,et al."Oxygen permeability and structural stability of BaCe0.15Fe0.85O3-delta membranes".journal of membrane science 283.1-2(2006):38-44. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论