Effects of Al-based additives on the hydrogen storage performance of the Mg(NH2)(2)-2LiH system | |
Cao, Hujun1,2,3; Zhang, Yao1; Wang, Jianhui1; Xiong, Zhitao1; Wu, Guotao1; Qiu, Jieshan2; Chen, Ping1,4 | |
刊名 | dalton transactions
![]() |
2013 | |
卷号 | 42期号:15页码:5524-5531 |
英文摘要 | the mg(nh2)(2)-2lih composite is a promising hydrogen storage material due to its relatively high reversible hydrogen capacity (similar to 5.6 wt%) and suitable thermodynamic properties that allow hydrogen sorption conducting at temperatures below 90 degrees c. however, the presence of a severe kinetic barrier inhibits its low-temperature operation. in the present work, li3alh6 was introduced to the mg(nh2)(2)-2lih system. experimental results show that a 3.2% mol li3alh6-modified mg(nh2)(2)-2lih sample released hydrogen at a rate ca. 4.5 times as fast as that of the li3alh6-free sample at 140 degrees c. the enhancement of desorption kinetics was simultaneously demonstrated by activation energy (e-a) of ca. 96.3 +/- 9 kj mol(-1) which was significantly decreased by 31 kj mol(-1) from that of the li3alh6-free sample. the interaction of li3alh6 and mg(nh2)(2) during ball milling results in the formation of lial(nh)(2), linh2 and mg3n2. lial(nh)(2) was actually the active species for the enhancement of dehydrogenation/re-hydrogenation kinetics of the system. |
WOS标题词 | science & technology ; physical sciences |
类目[WOS] | chemistry, inorganic & nuclear |
研究领域[WOS] | chemistry |
关键词[WOS] | n-h system ; thermal-decomposition ; crystal-structure ; li ; desorption ; absorption ; hydride ; libh4 ; lial(nh2)(4) ; improvement |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000316300700040 |
公开日期 | 2015-11-10 |
内容类型 | 期刊论文 |
源URL | [http://159.226.238.44/handle/321008/137849] ![]() |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian Natl Lab Clean Energy, Dalian 116023, Peoples R China 2.Dalian Univ Technol, Carbon Res Lab, Liaoning Key Lab Energy Mat & Chem Engn, State Key Lab Fine Chem, Dalian 116024, Peoples R China 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 4.Int Inst Carbon Neutral Energy Res I2CNER, Nishi Ku, Fukuoka 8190395, Japan |
推荐引用方式 GB/T 7714 | Cao, Hujun,Zhang, Yao,Wang, Jianhui,et al. Effects of Al-based additives on the hydrogen storage performance of the Mg(NH2)(2)-2LiH system[J]. dalton transactions,2013,42(15):5524-5531. |
APA | Cao, Hujun.,Zhang, Yao.,Wang, Jianhui.,Xiong, Zhitao.,Wu, Guotao.,...&Chen, Ping.(2013).Effects of Al-based additives on the hydrogen storage performance of the Mg(NH2)(2)-2LiH system.dalton transactions,42(15),5524-5531. |
MLA | Cao, Hujun,et al."Effects of Al-based additives on the hydrogen storage performance of the Mg(NH2)(2)-2LiH system".dalton transactions 42.15(2013):5524-5531. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论