Toughening of poly(propylene carbonate) using rubbery non-isocyanate polyurethane: Transition from brittle to marginally tough | |
Ren, Guanjie ; Sheng, Xingfeng ; Qin, Yusheng ; Chen,Xuesi ; Wang,Xianhong ; Wang,Fosong | |
刊名 | polymer |
2014 | |
卷号 | 55期号:21页码:5460-5468 |
关键词 | MICROMECHANICAL DEFORMATION PROCESSES FILLED SEMICRYSTALLINE POLYMERS HYDROGEN-BONDING INTERACTIONS MISCIBILITY ENHANCEMENT INFRARED TEMPERATURE PHASE-MORPHOLOGY IMPACT BEHAVIOR PROPYLENE-OXIDE PART 2 BLENDS |
通讯作者 | wang,xh |
英文摘要 | to overcome the brittleness of poly(propylene carbonate) (ppc), rubbery non-isocyanate polyurethane (nipu) with rich hydrogen bonding moiety was synthesized for toughening ppc. debonding phenomenon of nipu was observed during the impact process of ppc/nipu blends, which was beneficial for toughening ppc. when the nipu loading increased to 10 wt%, the unnotched impact strength increased 3 times compared with neat ppc. the nipu dispersed uniformly and a transition from brittle to marginally tough occurred when lid reached a critical value, 1.74, where l and d were center-to-center distance and the diameter of the particle, respectively. the debonding of nipu accounted for the increase of toughness, and shear yielding of the matrix was limited around the microvoids. when the nipu loading reached 13 wt%, nipu flocculated in the matrix leading to decline in toughness. the equilibrium between self-associating hydrogen bonding and intermolecular one formed between ppc and nipu affected their miscibility and thereby the morphology of the blends. (c) 2014 elsevier ltd. all rights reserved. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2015-10-27 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/57318] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Ren, Guanjie,Sheng, Xingfeng,Qin, Yusheng,et al. Toughening of poly(propylene carbonate) using rubbery non-isocyanate polyurethane: Transition from brittle to marginally tough[J]. polymer,2014,55(21):5460-5468. |
APA | Ren, Guanjie,Sheng, Xingfeng,Qin, Yusheng,Chen,Xuesi,Wang,Xianhong,&Wang,Fosong.(2014).Toughening of poly(propylene carbonate) using rubbery non-isocyanate polyurethane: Transition from brittle to marginally tough.polymer,55(21),5460-5468. |
MLA | Ren, Guanjie,et al."Toughening of poly(propylene carbonate) using rubbery non-isocyanate polyurethane: Transition from brittle to marginally tough".polymer 55.21(2014):5460-5468. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论