Super Tough, Ultrastretchable, and Thermoresponsive Hydrogels with Functionalized Triblock Copolymer Micelles as Macro-Cross-Linkers | |
Sun, Yuan-na ; Gao, Guo-rong ; Du, Gao-lai ; Cheng, Ya-jun ; Fu, Jun | |
刊名 | ACS MACRO LETTERS
![]() |
2014 | |
卷号 | 3期号:5页码:496 |
中文摘要 | Vinyl-functionalized thermosensitive Pluronic F127 micelles have been used as multifunctional cross-links for the synthesis of super tough, highly resilient and thermoresponsive nanomicelle (NM) hydrogels. Pluronic F127 diacrylate (F127DA) with vinyl groups on both ends self-assembled in aqueous solution into micelles. Such micelles served as multifunctional macro-cross-links to copolymerize with acrylamide (AAm) monomers, generating novel NM hydrogels with extraordinary tensile and compressive properties, without using any chemical cross-linkers. Uniaxial tensile tests demonstrated a fracture strain above 2265%, an ultimate stress of 276 kPa, and a fracture energy of 2.34 MJ/m(3). Under compression tests, these hydrogels did not fracture up to 98% strain and 62 MPa stress. Cyclic compressive loading unloading tests at 90% strain showed no decay of the hyseteresis energy, indicating an unprecedented fatigue resistance. |
公开日期 | 2015-09-20 |
内容类型 | 期刊论文 |
源URL | [http://ir.nimte.ac.cn/handle/174433/11855] ![]() |
专题 | 宁波材料技术与工程研究所_2014专题 |
推荐引用方式 GB/T 7714 | Sun, Yuan-na,Gao, Guo-rong,Du, Gao-lai,et al. Super Tough, Ultrastretchable, and Thermoresponsive Hydrogels with Functionalized Triblock Copolymer Micelles as Macro-Cross-Linkers[J]. ACS MACRO LETTERS,2014,3(5):496. |
APA | Sun, Yuan-na,Gao, Guo-rong,Du, Gao-lai,Cheng, Ya-jun,&Fu, Jun.(2014).Super Tough, Ultrastretchable, and Thermoresponsive Hydrogels with Functionalized Triblock Copolymer Micelles as Macro-Cross-Linkers.ACS MACRO LETTERS,3(5),496. |
MLA | Sun, Yuan-na,et al."Super Tough, Ultrastretchable, and Thermoresponsive Hydrogels with Functionalized Triblock Copolymer Micelles as Macro-Cross-Linkers".ACS MACRO LETTERS 3.5(2014):496. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论