Crystallization and Separation of Potassium Vanadate in Highly Concentrated Potassium Hydroxide Solution | |
Yang, N. ; Zheng, S. L. ; Wang, S. N. ; Qin, Y. L. ; Xie, W. L. ; Zhou, B. J. ; Zhang, Y. | |
2012 | |
会议名称 | International Conference on Chemical, Material and Metallurgical Engineering (ICCMME 2011) |
会议日期 | DEC 23-25, 2011 |
会议地点 | Beihai, PEOPLES R CHINA |
关键词 | Vanadium slag K3VO4 Crystallization Sub-Molten Salt VANADIUM |
页码 | 655-662 |
中文摘要 | The crystallization behavior of potassium vanadate from highly concentrated potassium hydroxide aqueous solution was investigated. The effect of various parameters including KOH concentration, V2O5 concentration, final crystallization temperature, cooling rate, stirring speed and additive amount of seed were examined. The optimal experimental conditions for K3VO4 crystallization were obtained as follows: KOH concentration 800 similar to 850 g/L, KOH-to-V2O5 mass ratio 8 similar to 9, stirring speed 200 r/min, crystallization temperature from 80 degrees C to 40 degrees C with natural cooling, and seed addition 2% wt. Under optimal conditions, the K3VO4 crystallization yield of 87% was obtained, and the purity of crystals was about 90%. |
收录类别 | CPCI |
会议网址 | |
会议录 | ADVANCES IN CHEMICAL ENGINEERING, PTS 1-3 丛书: Advanced Materials Research |
会议录出版者 | Trans Tech Publications Ltd |
语种 | 英语 |
内容类型 | 会议论文 |
源URL | [http://ir.ipe.ac.cn/handle/122111/11276] |
专题 | 过程工程研究所_研究所(批量导入) |
推荐引用方式 GB/T 7714 |
Yang, N.,Zheng, S. L.,Wang, S. N.,et al. Crystallization and Separation of Potassium Vanadate in Highly Concentrated Potassium Hydroxide Solution[C]. 见:International Conference on Chemical, Material and Metallurgical Engineering (ICCMME 2011). Beihai, PEOPLES R CHINA. DEC 23-25, 2011. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论