Preparation of MnOx-CeO2-Al2O3 mixed oxides for NOx-assisted soot oxidation: Activity, structure and thermal stability

CORC > 上海应用物理研究所 > 中国科学院上海应用物理研究所 > 中科院上海应用物理研究所2011-2017年

	Preparation of MnOx-CeO2-Al2O3 mixed oxides for NOx-assisted soot oxidation: Activity, structure and thermal stability
	Lin, Fan ; Wu, Xiaodong ; Liu, Shuang ; Weng, Duan ; Huang, Yuying
刊名	CHEMICAL ENGINEERING JOURNAL
	2013
卷号	226 页码:CONCATENATE(Sheet1!I260,-Sheet1!J260)
ISSN号	1385-8947
英文摘要	Three kinds of MnOx-CeO2-Al2O3 mixed oxides were prepared by introducing Al2O3 to MnOx-CeO2 at different stages of a sol-gel method. MnCeAl and MnCe/Al were received by adding aluminum nitrate and alumina powders to the Mn-Ce precursor solution, respectively, while MnCe + Al was obtained by mixing the sol-gel-synthesized MnOx-CeO2 and Al2O3 powders mechanically. The catalysts were calcined in air at 800 degrees C for 20 h to obtain the thermally aged samples. The catalysts were characterized by soot and NO temperature-programmed oxidation (soot-TPO and NO-TPO), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), extended X-ray absorption fine structure (EXAFS), energy dispersive spectroscopy (EDS) and H-2 temperature-programmed reduction (TPR). The introduction of Al2O3 degrades the soot oxidation activity of the fresh catalysts compared with MnOx-CeO2 mixed oxides, but it helps to maintain relatively high catalyst surface area and high MnOx dispersion after the rigorous aging treatment. Among the catalysts prepared, MnCe/Al exhibits the highest thermal stability with a small increase of T-m by 17 degrees C for soot oxidation after aging. The active surface area, which refers to the exposure area of MnOx on the catalyst, is suggested to determine the NO oxidation and soot oxidation activities of the aged catalysts. (C) 2013 Elsevier B.V. All rights reserved.
收录类别	SCI
语种	英语
WOS记录号	WOS:000321411800015
公开日期	2014-06-13
内容类型	期刊论文
源URL	[http://ir.sinap.ac.cn/handle/331007/13863]
专题	上海应用物理研究所_中科院上海应用物理研究所2011-2017年
推荐引用方式 GB/T 7714	Lin, Fan,Wu, Xiaodong,Liu, Shuang,et al. Preparation of MnOx-CeO2-Al2O3 mixed oxides for NOx-assisted soot oxidation: Activity, structure and thermal stability[J]. CHEMICAL ENGINEERING JOURNAL,2013,226:CONCATENATE(Sheet1!I260,-Sheet1!J260).
APA	Lin, Fan,Wu, Xiaodong,Liu, Shuang,Weng, Duan,&Huang, Yuying.(2013).Preparation of MnOx-CeO2-Al2O3 mixed oxides for NOx-assisted soot oxidation: Activity, structure and thermal stability.CHEMICAL ENGINEERING JOURNAL,226,CONCATENATE(Sheet1!I260,-Sheet1!J260).
MLA	Lin, Fan,et al."Preparation of MnOx-CeO2-Al2O3 mixed oxides for NOx-assisted soot oxidation: Activity, structure and thermal stability".CHEMICAL ENGINEERING JOURNAL 226(2013):CONCATENATE(Sheet1!I260,-Sheet1!J260).