Nanocasting synthesis of graphitized ordered mesoporous carbon using Fe-coated SBA-15 template

CORC > 生态环境研究中心 > 中国科学院生态环境研究中心 > 环境纳米材料实验室

	Nanocasting synthesis of graphitized ordered mesoporous carbon using Fe-coated SBA-15 template
	Li, Jinjun ; Liang, Yan ; Dou, Baojuan ; Ma, Chunyan ; Lu, Renjie ; Hao, Zhengping ; Xie, Qiang ; Luan, Zhiqiang ; Li, Kai
刊名	MATERIALS CHEMISTRY AND PHYSICS
	2013
卷号	138 期号:41673 页码:484-489
通讯作者	Li, JJ
中文摘要	Ordered mesoporous carbons with high porosities and graphitized structures were synthesized by a template-catalysis method using low-molecular-weight phenolic resin as carbon precursor and Fe-coated SBA-15 as both template and catalyst. The synthesis route involves the following steps: (a) the synthesis of mesoporous Fe-coated SBA-15 through a one-pot method, (b) the infiltration of a low-molecular-weight phenolic resin into the porosity of the Fe-coated SBA-15, (c) the carbonization and catalytic graphitization of the infiltrated phenolic resin at 900 degrees C, and (d) the removal of the Fe-coated SBA-15 template. The X-ray diffraction, nitrogen sorption, transmission electron microscopy and scanning electron microscopy were used to characterize the materials, and the results indicate that the prepared carbon materials have well-ordered mesoporous structures replicated from the templates, and graphitized structures can be observed on the carbon frameworks, depending on the iron content in the templates. (C) 2012 Elsevier B.V. All rights reserved.
收录类别	SCI
WOS记录号	WOS:000316580000012
公开日期	2014-06-05
内容类型	期刊论文
源URL	[http://ir.rcees.ac.cn/handle/311016/7347]
专题	生态环境研究中心_环境纳米材料实验室
推荐引用方式 GB/T 7714	Li, Jinjun,Liang, Yan,Dou, Baojuan,et al. Nanocasting synthesis of graphitized ordered mesoporous carbon using Fe-coated SBA-15 template[J]. MATERIALS CHEMISTRY AND PHYSICS,2013,138(41673):484-489.
APA	Li, Jinjun.,Liang, Yan.,Dou, Baojuan.,Ma, Chunyan.,Lu, Renjie.,...&Li, Kai.(2013).Nanocasting synthesis of graphitized ordered mesoporous carbon using Fe-coated SBA-15 template.MATERIALS CHEMISTRY AND PHYSICS,138(41673),484-489.
MLA	Li, Jinjun,et al."Nanocasting synthesis of graphitized ordered mesoporous carbon using Fe-coated SBA-15 template".MATERIALS CHEMISTRY AND PHYSICS 138.41673(2013):484-489.