SYNTHESIS AND CHARACTERATION OF POLY (ETHYLENE 2,5-FURANDICARBOXYLATE) | |
Jiang M ; Liu Q ; Li Y ; Zhang Q ; Zhou GY | |
刊名 | acta polymerica sinica
![]() |
2013 | |
期号 | 1页码:24-29 |
关键词 | RENEWABLE RESOURCES MECHANICAL-PROPERTIES FURAN |
ISSN号 | 1000-3304 |
通讯作者 | jiang m |
中文摘要 | poly(ethylene 2, 5-furandicarboxylate) (pef) was synthesized via direct esterification method based on 2, 5-furanicarboxylica acid and ethylene glycol. stannous oxalate was used as catalyst. the results showed that the direct esterification method was a straightforward and convenient effective way for preparing pef. the results of fourier transform infrared spectroscopy (ftir) and nuclear magnetic resonance spectroscopy (h-1-nmr) confirmed the expected pef structure. the results of ubbelohde viscosity method and gel permeation chromatography (gpc) declared the relationship between intrinsic viscosities and weight-average molecular weight was [eta] = 2.82 x 10(-6) m-w (0.99) [dl/g, 25 degrees c, phenol-tetrachloroethane (1: 1, w/w)]; the results of differential scanning calorimeter (dsc) displayed that the glass transition (t-g) of pef was 84 degrees c which was 16 k higher than that of poly(ethylene terephthalate) (pet) and the melting temperature (t-m) of pef was 211 degrees c which was 43 k lower than that of pet. the results of thermogravimetric analysis (tga) showed that the pef was thermally stable up to 373 degrees c pef had good thermal properties and was similar to that of pet. the results of coaxial cylinder viscometer showed that the pef melt was a pseudoplastic newtonian fluid and its non-newtonian index increased with decreasing of relative molecular weight and increasing of temperature. non-newtonian index was about 0.85 (melting temperature = 230 similar to 250 degrees c, rate of shear = 2.17 x 10(-2) similar to 1.14 x 10(2) s(-1)). |
收录类别 | SCI收录期刊论文 |
语种 | 中文 |
WOS记录号 | WOS:000314263500004 |
公开日期 | 2014-04-20 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/50498] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Jiang M,Liu Q,Li Y,et al. SYNTHESIS AND CHARACTERATION OF POLY (ETHYLENE 2,5-FURANDICARBOXYLATE)[J]. acta polymerica sinica,2013(1):24-29. |
APA | Jiang M,Liu Q,Li Y,Zhang Q,&Zhou GY.(2013).SYNTHESIS AND CHARACTERATION OF POLY (ETHYLENE 2,5-FURANDICARBOXYLATE).acta polymerica sinica(1),24-29. |
MLA | Jiang M,et al."SYNTHESIS AND CHARACTERATION OF POLY (ETHYLENE 2,5-FURANDICARBOXYLATE)".acta polymerica sinica .1(2013):24-29. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论