Preparation and characterization of MnFe2O4 in the solvothermal process: Their magnetism and electrochemical properties

	Preparation and characterization of MnFe2O4 in the solvothermal process: Their magnetism and electrochemical properties
	Lin XM ; Lv X ; Wang LM ; Zhang FF ; Duan LF
刊名	materials research bulletin
	2013
卷号	48 期号:7 页码:2511-2516
关键词	NANOPARTICLES LITHIUM ROUTE NANORODS CO3O4 NANOSTRUCTURES NANOCRYSTALS PERFORMANCE ALPHA-FE2O3 REDUCTION
ISSN号	0025-5408
通讯作者	duan lf
中文摘要	the uniform different morphologies mnfe2o4, including cube, truncated cube, polyhedron and octahedron, were successfully synthesized via a solvothermal route using cetyltrimethylammonium bromide. the results of control experiments revealed that the concentration of cetyltrimethylammonium bromide was an important factor, which affected the morphology and crystallization of mnfe2o4 submicro-crystals. all the prepared samples exhibited soft-magnetic behavior at room temperature. especially, the coercivity of mnfe2o4 polyhedron with 200 nm diameter was 11.9 oe, which was among the lowest values reported so far. moreover, mnfe2o4 submicro-crystals with special morphologies demonstrated higher reversible capacity (about 1000 mah g(-1)) and different cycle performances. after 50 cycles, polyhedron structure remained 428 mah/g. the mnfe2o4 would have a potential application as anode material for lithium ion batteries. (c) 2013 elsevier ltd. all rights reserved.
收录类别	SCI收录期刊论文
语种	英语
WOS记录号	WOS:000320073600015
公开日期	2014-04-15
内容类型	期刊论文
源URL	[http://ir.ciac.jl.cn/handle/322003/49762]
专题	长春应用化学研究所_长春应用化学研究所知识产出_期刊论文
推荐引用方式 GB/T 7714	Lin XM,Lv X,Wang LM,et al. Preparation and characterization of MnFe2O4 in the solvothermal process: Their magnetism and electrochemical properties[J]. materials research bulletin,2013,48(7):2511-2516.
APA	Lin XM,Lv X,Wang LM,Zhang FF,&Duan LF.(2013).Preparation and characterization of MnFe2O4 in the solvothermal process: Their magnetism and electrochemical properties.materials research bulletin,48(7),2511-2516.
MLA	Lin XM,et al."Preparation and characterization of MnFe2O4 in the solvothermal process: Their magnetism and electrochemical properties".materials research bulletin 48.7(2013):2511-2516.