Electrospinning fabrication and electrochemical properties of LiFePO4/C composite nanofibers | |
Shao DQ ; Wang JX ; Dong XT ; Yu WS ; Liu GX ; Zhang FF ; Wang LM | |
刊名 | journal of materials science-materials in electronics |
2013 | |
卷号 | 24期号:11页码:4263-4269 |
关键词 | CARBON-COATED LIFEPO4 HYDROTHERMAL SYNTHESIS LITHIUM BATTERIES PERFORMANCE NANOPARTICLES |
ISSN号 | 0957-4522 |
通讯作者 | dong xt |
中文摘要 | lifepo4/c composite nanofibers were synthesized by calcination of the [lioh + fe(no3)(3) + h3po4]/pvp electrospun nanofibers. polyvinyl pyrrolidone (pvp) was used as the electrospinning template and carbon source. during the calcination [lioh + fe(no3)(3) + h3po4] were transformed to lifepo4 and pvp was decomposed into carbon. the morphology and properties of the as-prepared samples were characterized by x-ray diffraction, scanning electron microscopy, transmission electron microscopy, brunauer-emmett-teller (bet) specific surface area analysis, electrochemical impedance spectroscopy and galvanostatic charge-discharge measurements. the results indicate that the mean diameter of as-prepared lifepo4/c composite nanofibers is 179.08 +/- a 29.66 nm and the bet specific surface area is 66.59 m(2) g(-1). the addition of carbon does not affect the structure of lifepo4, but improves its electrochemical performances. at the current density of 0.2 c, the initial discharge capacity of lifepo4/c electrode is 133.6 mah g(-1) and there is no obvious capacity fading after 100 cycles. the formation mechanism of the lifepo4/c composite nanofibers was also proposed. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000326047300020 |
公开日期 | 2014-04-15 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/49505] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Shao DQ,Wang JX,Dong XT,et al. Electrospinning fabrication and electrochemical properties of LiFePO4/C composite nanofibers[J]. journal of materials science-materials in electronics,2013,24(11):4263-4269. |
APA | Shao DQ.,Wang JX.,Dong XT.,Yu WS.,Liu GX.,...&Wang LM.(2013).Electrospinning fabrication and electrochemical properties of LiFePO4/C composite nanofibers.journal of materials science-materials in electronics,24(11),4263-4269. |
MLA | Shao DQ,et al."Electrospinning fabrication and electrochemical properties of LiFePO4/C composite nanofibers".journal of materials science-materials in electronics 24.11(2013):4263-4269. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论