Subsolidus phase relations of Bi2O3-Nd2O3-CuO | |
Sun, YZ ; Rao, GH ; Yang, JL ; Tang, WH ; Chen, XL ; Liang, JK | |
刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
![]() |
1997 | |
卷号 | 248期号:1-2页码:106 |
关键词 | SINTERED OXIDES DIFFRACTION POWDER ION CONDUCTION |
ISSN号 | 0925-8388 |
通讯作者 | Sun, YZ (reprint author), CHINESE ACAD SCI,INST PHYS,POB 603,BEIJING 100080,PEOPLES R CHINA. |
中文摘要 | The subsolidus phase relations of the Bi2O3-Nd2O3-CuO ternary system and its binary systems along with crystallographic parameters of the compounds were investigated by X-ray powder diffraction and differential thermal analysis. The room temperature section of the phase diagram of the Bi2O3-Nd2O3-CuO system can be divided into two diphase regions and six triphase regions. No ternary compound was found. There exist two solid solutions (alpha, beta) and a compound Bi0.55Nd0.45O1.5 in the (Bi2O2)(1-x)(Nd2O3)(x) system. Both solid solution alpha (0.05 less than or equal to x less than or equal to 10.30) and beta (0.53 less than or equal to x less than or equal to 0.73) belong to the rhombohedral system (R (3) over bar m). The lattice parameters represented by a hexagonal cell are a = 3.9832(4), c = 27.536(5) Angstrom for Bi0.8Nd0.2O1.5 (alpha phase) and a = 3.8826(3), c = 9.727(1) Angstrom for Bi0.4Nd0.8O1.5 (beta phase). The Bi0.55Nd0.45O1.5 compound crystallizes in a face-centered cubic (f.c.c.) lattice with a = 5.5480(2) Angstrom. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-24 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/53915] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Sun, YZ,Rao, GH,Yang, JL,et al. Subsolidus phase relations of Bi2O3-Nd2O3-CuO[J]. JOURNAL OF ALLOYS AND COMPOUNDS,1997,248(1-2):106. |
APA | Sun, YZ,Rao, GH,Yang, JL,Tang, WH,Chen, XL,&Liang, JK.(1997).Subsolidus phase relations of Bi2O3-Nd2O3-CuO.JOURNAL OF ALLOYS AND COMPOUNDS,248(1-2),106. |
MLA | Sun, YZ,et al."Subsolidus phase relations of Bi2O3-Nd2O3-CuO".JOURNAL OF ALLOYS AND COMPOUNDS 248.1-2(1997):106. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论