Significantly enhanced critical current densities in MgB2 tapes made by a scaleable nanocarbon addition route | |
Ma, YW ; Zhang, XP ; Nishijima, G ; Watanabe, K ; Awaji, S ; Bai, XD | |
刊名 | APPLIED PHYSICS LETTERS
![]() |
2006 | |
卷号 | 88期号:7 |
关键词 | MAGNESIUM DIBORIDE SUPERCONDUCTOR WIRES FIELD |
ISSN号 | 0003-6951 |
通讯作者 | Ma, YW (reprint author), Chinese Acad Sci, Appl Superconduct Lab, Inst Elect Engn, PO 2703, Beijing 100080, Peoples R China. |
中文摘要 | Nanocarbon-doped Fe-sheathed MgB2 tapes with different doping levels were prepared by the in situ powder-in-tube method. Compared to the undoped tapes, J(c) for all the C-doped samples was enhanced by more than an order of magnitude in magnetic fields above 9 T. At 4.2 K, the transport J(c) for the 5 at. % doped tapes reached 1.85x10(4) A/cm(2) at 10 T and 2.8x10(3) A/cm(2) at 14 T, respectively. Moreover, the critical temperature for the doped tapes decreased slightly. Transmission electron microscopy showed a number of intragranular dislocations and the dispersed nanoparticles embedded within MgB2 grains induced by the C doping. The mechanism for the enhancement of flux pinning is also discussed. These results indicate that powder-in-tube-processed MgB2 tape is very promising for high-field applications. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-24 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/52549] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Ma, YW,Zhang, XP,Nishijima, G,et al. Significantly enhanced critical current densities in MgB2 tapes made by a scaleable nanocarbon addition route[J]. APPLIED PHYSICS LETTERS,2006,88(7). |
APA | Ma, YW,Zhang, XP,Nishijima, G,Watanabe, K,Awaji, S,&Bai, XD.(2006).Significantly enhanced critical current densities in MgB2 tapes made by a scaleable nanocarbon addition route.APPLIED PHYSICS LETTERS,88(7). |
MLA | Ma, YW,et al."Significantly enhanced critical current densities in MgB2 tapes made by a scaleable nanocarbon addition route".APPLIED PHYSICS LETTERS 88.7(2006). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论