Magnetic phase transitions and magnetic properties of Nd-3(Fe,Mo)(29) compound and its nitride

CORC > 物理研究所 > 物理所公开发表论文 > 期刊论文

	Magnetic phase transitions and magnetic properties of Nd-3(Fe,Mo)(29) compound and its nitride
	Pan, HG ; Wang, XH ; Chen, Y ; Chen, CP ; Yang, FM
刊名	TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
	1998
卷号	8 期号:2 页码:211
关键词	CRYSTAL-STRUCTURE TERNARY PHASE ND SM GD ND3FE29-XTIX ANISOTROPY SYSTEM R=CE
ISSN号	1003-6326
中文摘要	Iron-rich ternary intermetallic compound Nd-3(Fe, Mo)(29) with the Nd-3(Fe, Ti)(29)-type monoclinic structure and its nitride were prepared. The intrinsic magnetic properties, magnetic phase transitions, and the magnetocrystalline anisotropy, have been investigated. The results show that the Curie temperature of Nd-3(Fe, Mo)(29) nitride is 675 K, which is 70.9 % higher than that of parent compound (395 K), the saturation magnetization as and anisotropy fields H-A are 151.0 Am-2/kg and 14.0 T at 4.2 K, 116.0 Am-2/kg and 1.6 T at 300 K for Nd-3(Fe, Mo)(29) compound, 161.0 Am-2/kg and 18.0 T at 4.2 K, 143.5 Am-2/kg and 4.2 T at 300 K for Nd-3(Fe, Mo)(29 )N-x nitride, respectively; the magnetocrystalline anisotropy of the Nd-3(Fe, Mo)(29) compound is planar above about 230 K and easy cone from 4.2 to 230 K, after nitrogenation, the spin reorientation phenomenon was no longer observed.
收录类别	SCI
语种	英语
公开日期	2013-09-18
内容类型	期刊论文
源URL	[http://ir.iphy.ac.cn/handle/311004/41275]
专题	物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式 GB/T 7714	Pan, HG,Wang, XH,Chen, Y,et al. Magnetic phase transitions and magnetic properties of Nd-3(Fe,Mo)(29) compound and its nitride[J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,1998,8(2):211.
APA	Pan, HG,Wang, XH,Chen, Y,Chen, CP,&Yang, FM.(1998).Magnetic phase transitions and magnetic properties of Nd-3(Fe,Mo)(29) compound and its nitride.TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,8(2),211.
MLA	Pan, HG,et al."Magnetic phase transitions and magnetic properties of Nd-3(Fe,Mo)(29) compound and its nitride".TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 8.2(1998):211.