IRRADIATION-INDUCED AMORPHIZATION OF THE AL76SI4MN20 ICOSAHEDRAL QUASI-CRYSTAL | |
WANG, RH ; TAKAHASHI, H ; OHNUKI, S ; WANG, ZG | |
刊名 | RADIATION EFFECTS AND DEFECTS IN SOLIDS
![]() |
1994 | |
卷号 | 129期号:3-4页码:173 |
关键词 | PHASE-TRANSITIONS AMORPHOUS PHASES AL-MN CRYSTALLINE |
ISSN号 | 1042-0150 |
通讯作者 | WANG, RH: WUHAN UNIV,DEPT PHYS,WUHAN 430072,PEOPLES R CHINA. |
中文摘要 | Irradiation effect of the Al76Si4Mn20 icosahedral quasicrystal (IQC) caused by 120 keV Ar ions and 1 MeV electrons has been studied by using transmission electron microscopy (TEM). The effect is dose and temperature dependent. At lower temperatures (less-than-or-equal-to345 K), Ar ions induces the Al-Si-Mn IQC fully amorphized. At medium temperature (352approximately400 K), only weak disordering and amorphization effects have been observed. At higher temperature (520approximately670 K) no measurable effect has been observed by TEM. The temperature ranges are shifted to much lower temperatures for 1 MeV electron irradiation. The Ar ion and electron dual irradiation possesses the same effect as Ar ion irradiation. Heating the amorphized specimen to 600approximately640 K induces it to transform to micro-quasicrystals and further heating to higher temperature (greater-than-or-equal-to660 K) induces crystallization. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-18 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/40395] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | WANG, RH,TAKAHASHI, H,OHNUKI, S,et al. IRRADIATION-INDUCED AMORPHIZATION OF THE AL76SI4MN20 ICOSAHEDRAL QUASI-CRYSTAL[J]. RADIATION EFFECTS AND DEFECTS IN SOLIDS,1994,129(3-4):173. |
APA | WANG, RH,TAKAHASHI, H,OHNUKI, S,&WANG, ZG.(1994).IRRADIATION-INDUCED AMORPHIZATION OF THE AL76SI4MN20 ICOSAHEDRAL QUASI-CRYSTAL.RADIATION EFFECTS AND DEFECTS IN SOLIDS,129(3-4),173. |
MLA | WANG, RH,et al."IRRADIATION-INDUCED AMORPHIZATION OF THE AL76SI4MN20 ICOSAHEDRAL QUASI-CRYSTAL".RADIATION EFFECTS AND DEFECTS IN SOLIDS 129.3-4(1994):173. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论