HEATING EFFECTS ON FINE-STRUCTURE OF A CU-AL-NI-MN-TI SHAPE-MEMORY ALLOY | |
ZOU, WH ; PENG, HY ; WANG, R ; GUI, J ; YANG, DZ | |
刊名 | ACTA METALLURGICA ET MATERIALIA |
1995 | |
卷号 | 43期号:8页码:3009 |
关键词 | MARTENSITE |
ISSN号 | 0956-7151 |
通讯作者 | ZOU, WH: WUHAN UNIV, DEPT PHYS, WUHAN 430072, PEOPLES R CHINA. |
中文摘要 | The heating effects on the structure and fine structure of Cu-11.9Al-5Ni-1.6Mn-1Ti (wt%) shape memory alloy have been studied by means of transmission electron microscopy and microscopic compositional analysis. With the increase of the heating temperature and time, the stabilized M18R(1) martensite, transformed from the parent phase of L2(1) structure type, underwent the following structural variations: M18R(1) --> N18R(1) --> disorder N9R. Disorder N9R bainite precipitates and retained parent phases were observed in specimens heated at 573 and 623 K for 7.2 ks or longer. When the alloy was heated at 673 K for 133.2 ks, equilibrium alpha, gamma(2) and Ni,Al-rich phases were formed without any retained beta(1) parent phase. While the size of the X(s) particles decreased in the specimen heated at 623 K for 7.2 ks and they disappeared completely in the specimen heated at 673 K, the X(L) particles were coarsened after heating. With the increase of the heating temperature and time the growth of the antiphase domains was observed. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/39122] |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | ZOU, WH,PENG, HY,WANG, R,et al. HEATING EFFECTS ON FINE-STRUCTURE OF A CU-AL-NI-MN-TI SHAPE-MEMORY ALLOY[J]. ACTA METALLURGICA ET MATERIALIA,1995,43(8):3009. |
APA | ZOU, WH,PENG, HY,WANG, R,GUI, J,&YANG, DZ.(1995).HEATING EFFECTS ON FINE-STRUCTURE OF A CU-AL-NI-MN-TI SHAPE-MEMORY ALLOY.ACTA METALLURGICA ET MATERIALIA,43(8),3009. |
MLA | ZOU, WH,et al."HEATING EFFECTS ON FINE-STRUCTURE OF A CU-AL-NI-MN-TI SHAPE-MEMORY ALLOY".ACTA METALLURGICA ET MATERIALIA 43.8(1995):3009. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论