	Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment
	Zhou, YF ; Wang, JC ; Tang, LA ; Chen, NF ; Chen, WC
刊名	JOURNAL OF INORGANIC MATERIALS
	2004
卷号	19 期号:2 页码:283
关键词	DOPED BI12SIO20 CRYSTALS BI12GEO20
ISSN号	1000-324X
通讯作者	Zhou, YF: Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China.
中文摘要	Ce-doped Bi12SiO20 single crystal with size of phi10mm x 40mm was successfully grown in space on board of the spacecraft Shenzhou No.3. The surface morphology of space-grown crystal is different from that of ground-grown crystal The space- and ground-grown crystals were measured by X-ray rocking curves, absorption spectra and micro-Raman spectra. The results show that the quality of Ce-deped crystal grown in space is better than that of the ground-grown one. The effect of doping on optical properties of BSO grown in space is evident in comparison with the ground-grown crystal.
收录类别	SCI
语种	中文
公开日期	2013-09-17
内容类型	期刊论文
源URL	[http://ir.iphy.ac.cn/handle/311004/38954]
专题	物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文
推荐引用方式 GB/T 7714	Zhou, YF,Wang, JC,Tang, LA,et al. Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment[J]. JOURNAL OF INORGANIC MATERIALS,2004,19(2):283.
APA	Zhou, YF,Wang, JC,Tang, LA,Chen, NF,&Chen, WC.(2004).Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment.JOURNAL OF INORGANIC MATERIALS,19(2),283.
MLA	Zhou, YF,et al."Growth of CeO2 : Bi12SiO20 crystals in multi-position furnace(II) - Space growth experiment".JOURNAL OF INORGANIC MATERIALS 19.2(2004):283.