Epitaxial layered cobaltite NaxCoO2 thin films grown on planar and vicinal cut substrates | |
Yu, L ; Gu, L ; Wang, Y ; Zhang, PX ; Habermeier, HU | |
刊名 | JOURNAL OF CRYSTAL GROWTH
![]() |
2011 | |
卷号 | 328期号:1页码:34 |
关键词 | PULSED-LASER DEPOSITION YBA2CU3O7-DELTA FILMS TRANSPORT-PROPERTIES SUPERCONDUCTIVITY ANISOTROPY |
ISSN号 | 0022-0248 |
通讯作者 | Yu, L: Kunming Univ Sci & Technol, Inst Adv Mat Photoelectrons, Kunming 650051, Peoples R China. |
中文摘要 | Epitaxial layered cobaltite Na0.5-0.7CoO2 thin films have been grown on planar SrTiO3 (1 0 0), SrTiO3 (1 1 0), LaAlO3 (1 0 0) and alpha-Al2O3 (0 0 0 1) substrates successfully by pulse laser deposition. The annealing temperature to influence of the crystal structure, surface morphology and electrical transport properties of NaxCoO2 thin films has been investigated. The layered structure of NaxCoO2 film and the interface between the film and substrate have been observed clearly by high resolution transmission electron microscopy. Vicinal cut SrTiO3 (1 0 0) substrates with the c-axis tilted angle theta 3-10 degrees have been used to grow NaxCoO2 thin films, which reveals that the c-axis orientation epitaxial growth on vicinal cut SrTiO3 (1 0 0) substrates only occurred when tilted angle theta <= 5 degrees. (C) 2011 Elsevier B.V. All rights reserved. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/37533] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Yu, L,Gu, L,Wang, Y,et al. Epitaxial layered cobaltite NaxCoO2 thin films grown on planar and vicinal cut substrates[J]. JOURNAL OF CRYSTAL GROWTH,2011,328(1):34. |
APA | Yu, L,Gu, L,Wang, Y,Zhang, PX,&Habermeier, HU.(2011).Epitaxial layered cobaltite NaxCoO2 thin films grown on planar and vicinal cut substrates.JOURNAL OF CRYSTAL GROWTH,328(1),34. |
MLA | Yu, L,et al."Epitaxial layered cobaltite NaxCoO2 thin films grown on planar and vicinal cut substrates".JOURNAL OF CRYSTAL GROWTH 328.1(2011):34. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论