Electrodeposition of Sb2Se3 on indium-doped tin oxides substrate: Nucleation and growth | |
Shi, XZ ; Zhang, X ; Tian, Y ; Shen, CM ; Wang, CM ; Gao, HJ | |
刊名 | APPLIED SURFACE SCIENCE
![]() |
2012 | |
卷号 | 258期号:6页码:2169 |
关键词 | THIN-FILMS OPTICAL-PROPERTIES DEPOSITION SEMICONDUCTORS N-SI(111) GOLD BATH |
ISSN号 | 0169-4332 |
通讯作者 | Wang, CM: Lanzhou Univ, Coll Chem & Engn, Tianshui S Rd 222, Lanzhou 730000, Peoples R China. |
中文摘要 | The mechanisms related to the initial stages of the nucleation and growth of antimony selenide (Sb2Se3) semiconductor compounds onto the indium-doped tin oxides (ITO) coated glass surface have been investigated using chronoamperometry (CA) technique. The fabrication was conducted from nitric acid bath containing both Sb3+ and SeO2 species at ambient conditions. No underpotential deposition (UPD) of antimony and selenium onto ITO substrate was observed in the investigated systems indicating a weak precursor-substrate interaction. Deposition of antimony and selenium onto ITO substrate occurred with large overvoltage through 3D nucleation and growth mechanism followed by diffusion limited growth. FE-SEM and XRD results show that orthorhombic phase Sb2Se3 particles with their size between 90 and 125 nm were obtained and the atomic ratio for antimony and selenium was 2:2.63 according to the EDX results. (C) 2011 Elsevier B.V. All rights reserved. |
收录类别 | SCI |
资助信息 | Special Doctoral Foundation of the Ministry Education of China [20775030]; National Natural Science Foundation of China [50872147]; 863 Program [2007AA03Z305] |
语种 | 英语 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/37026] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Shi, XZ,Zhang, X,Tian, Y,et al. Electrodeposition of Sb2Se3 on indium-doped tin oxides substrate: Nucleation and growth[J]. APPLIED SURFACE SCIENCE,2012,258(6):2169. |
APA | Shi, XZ,Zhang, X,Tian, Y,Shen, CM,Wang, CM,&Gao, HJ.(2012).Electrodeposition of Sb2Se3 on indium-doped tin oxides substrate: Nucleation and growth.APPLIED SURFACE SCIENCE,258(6),2169. |
MLA | Shi, XZ,et al."Electrodeposition of Sb2Se3 on indium-doped tin oxides substrate: Nucleation and growth".APPLIED SURFACE SCIENCE 258.6(2012):2169. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论