Effect of temperature on nonlinear electrical behavior and dielectric properties of (Ca, Ta)-doped TiO2 ceramics | |
Wang, WY ; Zhang, DF ; Xu, T ; Li, XF ; Zhou, T ; Chen, XL | |
刊名 | MATERIALS RESEARCH BULLETIN
![]() |
2002 | |
卷号 | 37期号:6页码:1197 |
关键词 | ZINC-OXIDE VARISTORS CAPACITOR SYSTEM |
ISSN号 | 0025-5408 |
通讯作者 | Wang, WY: Chinese Acad Sci, Inst Phys, POB 603-23, Beijing 100080, Peoples R China. |
中文摘要 | Polymer electrolytes composed of polyacrylonitrile (PAN), propylene carbonate (PC), and lithium bis(trifluoromethane sulfone imide) [LiTFSI, LiN(CF3SO2)(2)] have been studied by Raman and ac impedance spectroscopy. It is found that the associations of Li+ ions with the polymer and with the solvent are two separate procedures. This makes it possible to study the influences of the polymer and the salt content on the conductivity seperately. Impedance study shows that the conductivity of the electrolyte is strongly dependent on the salt content, and a transition from "salt-in-polymer'' to "polymer-in-salt'' electrolyte is observed when the salt content is very high (at PC: PAN: LiTFSI 5 1: 1: 4 mole ratio). Raman spectroscopic study indicates that the interactions between the lithium ionic species and the polymer are striking after PAN is dissolved in the PC/LiTFSI solution. A new spectral component is observed at 2280 cm(-1) involving the interaction between the polymer and ionic cluster [Lim+TFSIn-] (m > n) (at PC: PAN: LiTFSI = 1:1:3) as well as the 2270 cm(-1) peak due to the nitrile-Li+ interaction. As the interaction between PAN and the ionic clusters and the transition of conduction behavior occur at a similar salt content, it is proposed that PAN plays distinct roles in the transportation of the ionic species in conventional "salt-in-polymer'' electrolyte and in the novel "polymer-in-salt'' electrolytes. (C) 2002 The Electrochemical Society. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/36584] ![]() |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Wang, WY,Zhang, DF,Xu, T,et al. Effect of temperature on nonlinear electrical behavior and dielectric properties of (Ca, Ta)-doped TiO2 ceramics[J]. MATERIALS RESEARCH BULLETIN,2002,37(6):1197. |
APA | Wang, WY,Zhang, DF,Xu, T,Li, XF,Zhou, T,&Chen, XL.(2002).Effect of temperature on nonlinear electrical behavior and dielectric properties of (Ca, Ta)-doped TiO2 ceramics.MATERIALS RESEARCH BULLETIN,37(6),1197. |
MLA | Wang, WY,et al."Effect of temperature on nonlinear electrical behavior and dielectric properties of (Ca, Ta)-doped TiO2 ceramics".MATERIALS RESEARCH BULLETIN 37.6(2002):1197. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论