Approaches to improving critical current density of YBCO superconducting thick films deposited by electrophoresis | |
Zhu, YB ; Zhou, YL ; Liu, Z ; Wang, SF ; Chen, ZH ; Lu, HB ; Yang, GZ ; Xiao, L ; Ren, HT ; Jiao, YL ; Zheng, MH | |
刊名 | SCIENCE IN CHINA SERIES G-PHYSICS ASTRONOMY |
2004 | |
卷号 | 47期号:2页码:165 |
关键词 | YBA2CU3O7-X FILMS FABRICATION TAPES |
ISSN号 | 1672-1799 |
通讯作者 | Zhu, YB: Beijing Jiaotong Univ, Coll Sci, Dept Phys, Beijing 100044, Peoples R China. |
中文摘要 | Fabrication of YBCO superconducting thick films by electrophoresis has been widely reported. However, the value of critical current density (Jc) is far from what the practical application requires. The superconducting thick films are obtained using top-seeded melt growth method with different proportional Y2BaCuO5 (Y211) addition. High-pressure oxygen has been used in the annealing process to improve the uniformity of the oxygen content in the superconducting thick films. When 40mol% Y211 powder is added to the YBa2Cu3O7-delta (Y123) powder, J(c) for the superconducting thick film by approaches described above reaches 7.008x10(3) A/cm(2) (77 K, 0 T), which is greater than the value ever reported. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/33954] |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Zhu, YB,Zhou, YL,Liu, Z,et al. Approaches to improving critical current density of YBCO superconducting thick films deposited by electrophoresis[J]. SCIENCE IN CHINA SERIES G-PHYSICS ASTRONOMY,2004,47(2):165. |
APA | Zhu, YB.,Zhou, YL.,Liu, Z.,Wang, SF.,Chen, ZH.,...&Zheng, MH.(2004).Approaches to improving critical current density of YBCO superconducting thick films deposited by electrophoresis.SCIENCE IN CHINA SERIES G-PHYSICS ASTRONOMY,47(2),165. |
MLA | Zhu, YB,et al."Approaches to improving critical current density of YBCO superconducting thick films deposited by electrophoresis".SCIENCE IN CHINA SERIES G-PHYSICS ASTRONOMY 47.2(2004):165. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论