Synthesis of High-Purity Ti3SiC2 by Microwave Sintering

CORC > 宁波材料技术与工程研究所 > 中国科学院宁波材料技术与工程研究所 > 宁波所知识产出

	Synthesis of High-Purity Ti3SiC2 by Microwave Sintering
	Hu CF(胡春峰) ; Qian Wang ; Chunfeng Hu* and Qing Huang ; Shu Cai ; Yoshio Sakka ; Salvatore Grasso
刊名	Int. J. Appl. Ceram. Technol
	2013-10-16
期号	2 页码:1—8
通讯作者	胡春峰
合作状况	李雨桐
中文摘要	High-purity ternary laminated compound Ti3SiC2 was successfully synthesized by a microwave heating method in the flowing argon for the first time. The mixtures of titanium, silicon, and graphitic carbon (Cgc) or activated carbon (Cac) with different molar ratios were used to investigate the reaction mechanisms. It was confirmed that Ti3SiC2 with high purity of 98 vol.% was achieved without the aids of Al. The optimum experimental parameters were determined as Ti/Si/Cgc having the molar ratio of 3/2.2/2, first holding at 1480°C for 30 min, and subsequent dwelling at 1300°C for 60 min
学科主题	材料科学
原文出处	SCI收录
公开日期	2013-12-16
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/10067]
专题	宁波材料技术与工程研究所_宁波所知识产出
推荐引用方式 GB/T 7714	Hu CF,Qian Wang,Chunfeng Hu* and Qing Huang,et al. Synthesis of High-Purity Ti3SiC2 by Microwave Sintering[J]. Int. J. Appl. Ceram. Technol,2013(2):1—8.
APA	Hu CF,Qian Wang,Chunfeng Hu* and Qing Huang,Shu Cai,Yoshio Sakka,&Salvatore Grasso.(2013).Synthesis of High-Purity Ti3SiC2 by Microwave Sintering.Int. J. Appl. Ceram. Technol(2),1—8.
MLA	Hu CF,et al."Synthesis of High-Purity Ti3SiC2 by Microwave Sintering".Int. J. Appl. Ceram. Technol .2(2013):1—8.