Synthesis of thin amine-functionalized MIL-53 membrane with high hydrogen permeability | |
Chen L(陈亮) ; Haiyan Fan a,b, Haiping Xia a, Chunlong Kong b,**, Liang Chen b,* | |
刊名 | Intl. J. Hydrogen Energy
![]() |
2013-08-21 | |
期号 | 25页码:10795—10801 |
通讯作者 | 陈亮 |
合作状况 | 李雨桐 |
中文摘要 | A thin amine-functionalized MIL-53 membrane with high permeability of hydrogen was successfully prepared on a porous a-Al2O3 support by using the secondary growth method. Seeded a-Al2O3 supports were prepared by a dip-coating technique. In contrast, a discontinuous membrane was obtained by using unseeded support under the same synthesis conditions, implying that the seeds play the key role in the formation of compact membranes. The resulting compact membranes were measured by X-ray diffraction (XRD), scanning electron microscopy (SEM) and single gas permeation testing. Results showed that the thickness of the as-prepared membrane was around 2 w 4 mm. Hydrogen permeance of the as-prepared membrane reached a remarkable value of 1.5 10 5 mol m 2 s 1$Pa 1 at room temperature under a 0.1 MPa pressure drop. The ideal H2/CO2 selectivity was found to be 4.4. In addition, the influence of seeding solution on the membrane performance was investigated. We found that the membrane permeance decreased and the ideal selectivity increased when the seeding solution content was increased. |
学科主题 | 物理化学 |
原文出处 | SCI收录 |
公开日期 | 2013-12-16 |
内容类型 | 期刊论文 |
源URL | [http://ir.nimte.ac.cn/handle/174433/10011] ![]() |
专题 | 宁波材料技术与工程研究所_宁波所知识产出 |
推荐引用方式 GB/T 7714 | Chen L,Haiyan Fan a,b, Haiping Xia a, Chunlong Kong b,**, Liang Chen b,*. Synthesis of thin amine-functionalized MIL-53 membrane with high hydrogen permeability[J]. Intl. J. Hydrogen Energy,2013(25):10795—10801. |
APA | Chen L,&Haiyan Fan a,b, Haiping Xia a, Chunlong Kong b,**, Liang Chen b,*.(2013).Synthesis of thin amine-functionalized MIL-53 membrane with high hydrogen permeability.Intl. J. Hydrogen Energy(25),10795—10801. |
MLA | Chen L,et al."Synthesis of thin amine-functionalized MIL-53 membrane with high hydrogen permeability".Intl. J. Hydrogen Energy .25(2013):10795—10801. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论