Effect of sintering aids on mechanical properties and microstructure of alumina ceramic via stereolithography | |
Qian, Chuchu1,5; Hu, Kehui1,2,5; Shen, Zhen3; Wang, Qing4; Li, Peijie1,5; Lu, Zhigang1,2,5 | |
刊名 | CERAMICS INTERNATIONAL |
2023-06-01 | |
卷号 | 49期号:11页码:17506-17523 |
关键词 | Stereolithography Alumina additive manufacturing Sintering aids Mechanical properties Microstructure |
ISSN号 | 0272-8842 |
DOI | 10.1016/j.ceramint.2023.02.118 |
通讯作者 | Hu, Kehui(hukehui@tsinghua.edu.cn) |
英文摘要 | In this study, the effects of sintering aids (CaO, TiO2, La2O3 and ZrO2) on the physical and mechanical properties and microstructure of alumina ceramics made by stereolithography were systematically investigated. The addition of 3% CaO promoted internal porous structure at high temperatures, increasing the possibility of interlayer microcracking along the inner pores. 0.5% TiO2 had the best bending strength enhancement of alumina, increasing from 110.4 MPa to 201.1 MPa at a sintering temperature of 1650 degrees C. La2O3 took effect after 1550 degrees C and basically had no effect on refining grains. 1% ZrO2 increased 15% apparent porosity and 88% interlayer shear strength and reduced sintering shrinkage by about 30%, while maintaining bending strength. Optimised alumina powder ingredients and sintering conditions that could meet the performance index requirements of the ceramic core were obtained: particle size distribution 10 mu m/2 mu m (the mass fraction ratio of coarse to fine particles was 6:4), solid content 55%, sintering aid 1% ZrO2, sintering temperature 1450 degrees C. |
资助项目 | National Natural Science Foundation of China[52175333] ; National Science and Technology Major Project of China[J2019 -VII -0002] ; Foshan Science and Technology Innovation Team Project[2018IT100142] |
WOS关键词 | ABNORMAL GRAIN-GROWTH ; GAS-TURBINE BLADES ; TIO2 ; ADDITIVES ; FABRICATION ; DENSIFICATION ; EVOLUTION ; BEHAVIOR ; DENSITY ; PHASES |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000988523700001 |
资助机构 | National Natural Science Foundation of China ; National Science and Technology Major Project of China ; Foshan Science and Technology Innovation Team Project |
内容类型 | 期刊论文 |
源URL | [http://ir.ia.ac.cn/handle/173211/53338] |
专题 | 多模态人工智能系统全国重点实验室 |
通讯作者 | Hu, Kehui |
作者单位 | 1.Tsinghua Univ, State Key Lab Tribol, Beijing 100084, Peoples R China 2.Tsinghua Univ, Minist Educ, Key Lab Adv Mat Proc Technol, Beijing 100084, Peoples R China 3.Chinese Acad Sci, Inst Automat, State Key Lab Management & Control Complex Syst, Beijing 100190, Peoples R China 4.Ten Dimens Guangdong Technol Co Ltd, Foshan 528225, Peoples R China 5.Tsinghua Univ, Dept Mech Engn, Beijing 100084, Peoples R China |
推荐引用方式 GB/T 7714 | Qian, Chuchu,Hu, Kehui,Shen, Zhen,et al. Effect of sintering aids on mechanical properties and microstructure of alumina ceramic via stereolithography[J]. CERAMICS INTERNATIONAL,2023,49(11):17506-17523. |
APA | Qian, Chuchu,Hu, Kehui,Shen, Zhen,Wang, Qing,Li, Peijie,&Lu, Zhigang.(2023).Effect of sintering aids on mechanical properties and microstructure of alumina ceramic via stereolithography.CERAMICS INTERNATIONAL,49(11),17506-17523. |
MLA | Qian, Chuchu,et al."Effect of sintering aids on mechanical properties and microstructure of alumina ceramic via stereolithography".CERAMICS INTERNATIONAL 49.11(2023):17506-17523. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论