Toward Phi 56 mm Al-Polar AlN Single Crystals Grown by the Homoepitaxial PVT Method

doi:10.1021/acs.cgd.2c00240

CORC > 长春光学精密机械与物理研究所 > 中国科学院长春光学精密机械与物理研究所

	Toward Phi 56 mm Al-Polar AlN Single Crystals Grown by the Homoepitaxial PVT Method
	D. Y. Fu; D. Lei; Z. Li; G. Zhang; J. L. Huang; X. J. Sun; Q. K. Wang; D. B. Li; J. Wang and L. Wu
刊名	Crystal Growth & Design
	2022
卷号	22 期号:5 页码:3462-3470
ISSN号	1528-7483
DOI	10.1021/acs.cgd.2c00240
英文摘要	Crack-free and parasitic-free Al-polar aluminum nitride (AlN) single crystals up to Phi 56 mm were iteratively grown by the homoepitaxial physical vapor transport method. The detailed iterative growth processes from the spontaneous AlN boules to Phi 56 mm single crystals were presented. Our growth experiments revealed that stable growth of large Al-polar crystals with good structural quality and UV transparency was possible using a pure tungsten setup. For each iteration, the initial expansion angle, which was dominated by the radial temperature gradient (Delta T-r), reached 50-60 degrees under our specific growth system and growth conditions and then gradually decreased to 10-20 degrees during the growth process. For all as-grown crystals, mirror-like facets with a step-flow growth mode could be observed. However, the {10 (1) over bar0} side planes were strongly suppressed when using larger AlN seeds. Material characterization showed that the full width at half maximum of symmetric and asymmetric high-resolution X-ray diffraction rocking curves was 84-144 arcsec and 45-70 arcsec, respectively. The average etch pit density evaluated by preferential chemical etching was approximately 8.5 x 10(4) cm(-2). The optical transmission spectra revealed that the entire wafer exhibited excellent ultraviolet (UV) transparency, with absorption coefficients of 19-29 cm(-1) in the UV range of 4.43-4.77 eV (260-280 nm).
URL标识	查看原文
语种	英语
内容类型	期刊论文
源URL	[http://ir.ciomp.ac.cn/handle/181722/67188]
专题	中国科学院长春光学精密机械与物理研究所
推荐引用方式 GB/T 7714	D. Y. Fu,D. Lei,Z. Li,et al. Toward Phi 56 mm Al-Polar AlN Single Crystals Grown by the Homoepitaxial PVT Method[J]. Crystal Growth & Design,2022,22(5):3462-3470.
APA	D. Y. Fu.,D. Lei.,Z. Li.,G. Zhang.,J. L. Huang.,...&J. Wang and L. Wu.(2022).Toward Phi 56 mm Al-Polar AlN Single Crystals Grown by the Homoepitaxial PVT Method.Crystal Growth & Design,22(5),3462-3470.
MLA	D. Y. Fu,et al."Toward Phi 56 mm Al-Polar AlN Single Crystals Grown by the Homoepitaxial PVT Method".Crystal Growth & Design 22.5(2022):3462-3470.