In-situ CT characterization of 2D woven SiCf/SiC composite loading under compression | |
Guo, Weina2; Gao, Yantao2; Sun LJ(孙立娟)1 | |
刊名 | SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS
![]() |
2022-11-11 | |
卷号 | 29期号:1页码:394-402 |
关键词 | SiCf SiC composite in-situ CT microstructure damage evolution |
ISSN号 | 0792-1233 |
DOI | 10.1515/secm-2022-0166 |
通讯作者 | Gao, Yantao(gaoyantao@sues.edu.cn) |
英文摘要 | SiC fiber-reinforced SiC matrix composites (SiCf/SiC) with 2D woven fabric as preform were tested under compression with in-situ X-ray computed tomography. The microstructure and damage evolution of the material under continuous loading levels were accurately revealed by image reconstruction of CT data. There were inhomogeneous pores in SiCf/SiC composite because of the un-uniform fiber distribution in the preform. The result also showed that 2D woven SiCf/SiC composite had obvious non-linear characteristics by its compressive load-displacement curve, and the damage modes included transverse matrix cracking, interlayer cracking, longitudinal matrix cracking, and fiber bundle fracture. Matrix cracking tended to occur near the pores or holes of the material, and the number of longitudinal cracks was relatively high compared to the number of transverse cracks. |
分类号 | Q4 |
WOS关键词 | RAY TOMOGRAPHIC CHARACTERIZATION ; SILICON-CARBIDE FIBER ; SIC/SIC COMPOSITES ; MULTIPLE CRACKING ; DAMAGE ; FRACTURE ; MINICOMPOSITES ; FRAGMENTATION ; BEHAVIOR ; BRITTLE |
WOS研究方向 | Materials Science |
语种 | 英语 |
WOS记录号 | WOS:000881930900001 |
其他责任者 | Gao, Yantao |
内容类型 | 期刊论文 |
源URL | [http://dspace.imech.ac.cn/handle/311007/90798] ![]() |
专题 | 力学研究所_流固耦合系统力学重点实验室(2012-) |
作者单位 | 1.Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing, Peoples R China 2.Shanghai Univ Engn Sci, Sch Text & Fash, Shanghai 201620, Peoples R China; |
推荐引用方式 GB/T 7714 | Guo, Weina,Gao, Yantao,Sun LJ. In-situ CT characterization of 2D woven SiCf/SiC composite loading under compression[J]. SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS,2022,29(1):394-402. |
APA | Guo, Weina,Gao, Yantao,&孙立娟.(2022).In-situ CT characterization of 2D woven SiCf/SiC composite loading under compression.SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS,29(1),394-402. |
MLA | Guo, Weina,et al."In-situ CT characterization of 2D woven SiCf/SiC composite loading under compression".SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS 29.1(2022):394-402. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论