Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion | |
Sun, Congtao2,3; Sun, Ming2,3; Liu, Junde1; Dong, Zhenping1; Fan, Liang2,3; Duan, Jizhou2,3 | |
刊名 | MATERIALS |
2022-08-01 | |
卷号 | 15期号:15页码:12 |
关键词 | anti-corrosion performance MCIs reinforced concrete chloride erosion steel bar |
DOI | 10.3390/ma15155138 |
通讯作者 | Sun, Congtao(suncongtao@qdio.ac.cn) ; Dong, Zhenping(dongzp_02@163.com) |
英文摘要 | This study investigated the anti-corrosion performance of commercial amino alcohol migratory corrosion inhibitors (MCIs) on concrete that underwent varying degrees of chloride erosion. Electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PD), scanning electron microscopy, and energy dispersive spectroscopy (SEM-EDS) analyses were performed to study the anti-corrosion performance and mechanism of the MCIs on the steel bars. The results indicated that the corrosion resistance of the steel bars in concrete was significantly improved by coating with the MCIs, and the earlier the specimens were coated with the MCIs, the higher the anti-corrosion efficiency. The anti-corrosion efficiency was 55.35% when the MCIs coating was applied before chloride erosion; however, the anti-corrosion efficiency decreased to 3.40% when the MCIs coating was applied after the ninth drying-wetting cycle. The improvement in corrosion resistance of the steel bar in concrete coated with MCIs was due to the protective MCIs-molecule film that formed on the steel bar surfaces, and the oxidative dissolution of iron at the anode was effectively inhibited by the MCIs coating. |
资助项目 | National Natural Science Foundation of China[41827805] ; Natural Science Key Foundation of Shandong Province[ZR2020KE046] ; Strategic Priority Project of CAS[XDA13040402] |
WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering ; Physics |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000839206100001 |
内容类型 | 期刊论文 |
源URL | [http://ir.qdio.ac.cn/handle/337002/179937] |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
通讯作者 | Sun, Congtao; Dong, Zhenping |
作者单位 | 1.Xian Univ Architecture & Technol, Sch Civil Engn, Xian 710055, Peoples R China 2.Pilot Natl Lab Marine Sci & Technol Qingdao, Open Studio Marine Corros & Protect, Qingdao 266237, Peoples R China 3.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China |
推荐引用方式 GB/T 7714 | Sun, Congtao,Sun, Ming,Liu, Junde,et al. Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion[J]. MATERIALS,2022,15(15):12. |
APA | Sun, Congtao,Sun, Ming,Liu, Junde,Dong, Zhenping,Fan, Liang,&Duan, Jizhou.(2022).Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion.MATERIALS,15(15),12. |
MLA | Sun, Congtao,et al."Anti-Corrosion Performance of Migratory Corrosion Inhibitors on Reinforced Concrete Exposed to Varying Degrees of Chloride Erosion".MATERIALS 15.15(2022):12. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论