Effects of Pouring Temperature on Microstructure and Mechanical Properties of the A356 Aluminum Alloy Diecastings | |
Li, Ming1,3; Li, Yuandong2; Zhou, Hongwei2 | |
刊名 | MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS |
2020 | |
卷号 | 23期号:1 |
关键词 | Semisolid Self-Inoculation Method Primary alpha-Al Grain Secondary alpha-Al Grain Eutectic Si Mechanical Property |
ISSN号 | 1516-1439 |
DOI | 10.1590/1980-5373-MR-2019-0676 |
英文摘要 | Diecastings of the A356 aluminum alloy were produced by rheo-diecasting (RDC) and High pressure die casting (HPDC), the microstructures of primary solidification, secondary solidification and eutectic Si of diecastings with different pouring temperature were explored and the mechanical properties of different parameters were tested. The result shows that the primary alpha-Al grains in RDC with self-inoculation method (SIM) are smaller and rounder than the dendrite structure in HPDC. During the RDC process, the amount of primary alpha-Al grains, average grain size and the lamellar spacing of the eutectic Si increase with the decrease of the melt treatment temperature. While the average grain size and the shape factor are gradually increasing with the increase of melt treatment temperature. As a result, RDC can significantly improve the mechanical properties of the A356 aluminum alloy compared with HPDC, the mechanical properties are optimal at 600 degrees C with the tensile strength and elongation are 268.67MPa and 6.8%, respectively. |
资助项目 | National Natural Science Foundation of China[51464031] ; Youth Foundation of Hexi University[QN2018011] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | UNIV FED SAO CARLOS, DEPT ENGENHARIA MATERIALS |
WOS记录号 | WOS:000524064300001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/60009] |
专题 | 发展规划处 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Li, Ming |
作者单位 | 1.Hexi Univ, Inst Adv Mat Forming Technol, Zhangye 734000, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China 3.Hexi Univ, Zhangye 734000, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Ming,Li, Yuandong,Zhou, Hongwei. Effects of Pouring Temperature on Microstructure and Mechanical Properties of the A356 Aluminum Alloy Diecastings[J]. MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS,2020,23(1). |
APA | Li, Ming,Li, Yuandong,&Zhou, Hongwei.(2020).Effects of Pouring Temperature on Microstructure and Mechanical Properties of the A356 Aluminum Alloy Diecastings.MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS,23(1). |
MLA | Li, Ming,et al."Effects of Pouring Temperature on Microstructure and Mechanical Properties of the A356 Aluminum Alloy Diecastings".MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS 23.1(2020). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论