Mechanical properties and tensile fracture mechanism investigation of Al/Cu/Ti/Cu/Al laminated composites fabricated by rolling

doi:10.1016/j.jallcom.2019.07.064

CORC > 兰州理工大学 > 兰州理工大学 > 省部共建有色金属先进加工与再利用国家重点实验室

	Mechanical properties and tensile fracture mechanism investigation of Al/Cu/Ti/Cu/Al laminated composites fabricated by rolling
	Zhang, Xiaobo 1; Yu, Yangbo 1; Liu, Bin 2; Ren, Junqiang 1
刊名	JOURNAL OF ALLOYS AND COMPOUNDS
	2019-10-15
卷号	805 页码:338-345
关键词	Laminated composite Interface bonding Rolling Fracture Al/Cu/Ti
ISSN号	0925-8388
DOI	10.1016/j.jallcom.2019.07.064
英文摘要	Al/Cu/Ti/Cu/Al laminated composites were fabricated successfully by rolling with various rolling reduction at room temperature. It was found that the size of interior layer and Ti layer decreased gradually with the increasing of rolling reduction. The hardness values of Al, Cu and Ti layers increased linearly as the rolling reduction increased. The tensile tests showed that the larger rolling reduction was beneficial for the tensile strength increase, but the elongation decreased. The ultimate tensile stress of composite with 85% rolling reduction was 233 MPa. In-situ tensile test indicated that the crack initiated and propagated at Al/Cu interface. Due to the weak interface bonding strength and different plastic deformation capacity, the Al/Cu interface delaminated and the composites finally fractured. (C) 2019 Elsevier B.V. All rights reserved.
资助项目	National Natural Science Foundation of China (NSFC)[51601084]
WOS研究方向	Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	ELSEVIER SCIENCE SA
WOS记录号	WOS:000482184100037
状态	已发表
内容类型	期刊论文
源URL	[http://119.78.100.223/handle/2XXMBERH/31501]
专题	省部共建有色金属先进加工与再利用国家重点实验室
通讯作者	Zhang, Xiaobo
作者单位	1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Dept Mat Sci & Engn, Lanzhou 730050, Gansu, Peoples R China 2.State Key Lab Cemented Carbide, Zhuzhou 412000, Hunan, Peoples R China
推荐引用方式 GB/T 7714	Zhang, Xiaobo,Yu, Yangbo,Liu, Bin,et al. Mechanical properties and tensile fracture mechanism investigation of Al/Cu/Ti/Cu/Al laminated composites fabricated by rolling[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2019,805:338-345.
APA	Zhang, Xiaobo,Yu, Yangbo,Liu, Bin,&Ren, Junqiang.(2019).Mechanical properties and tensile fracture mechanism investigation of Al/Cu/Ti/Cu/Al laminated composites fabricated by rolling.JOURNAL OF ALLOYS AND COMPOUNDS,805,338-345.
MLA	Zhang, Xiaobo,et al."Mechanical properties and tensile fracture mechanism investigation of Al/Cu/Ti/Cu/Al laminated composites fabricated by rolling".JOURNAL OF ALLOYS AND COMPOUNDS 805(2019):338-345.