Investigation of Erosion-corrosion of Carbon Steel Elbow in 3.5% Sodium Chloride Containing Quartz | |
Hu, Zongwu1; Xing, Rui2; Liu, Jianguo3 | |
刊名 | INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE |
2022 | |
卷号 | 17期号:1 |
关键词 | Liquid-solid flow 90 horizontal elbow erosion-corrosion interaction |
ISSN号 | 1452-3981 |
DOI | 10.20964/2022.01.25 |
英文摘要 | In this study, the erosion-corrosion (E-C) behavior at different locations of a 90 degrees horizontal elbow was investigated under the condition of liquid-solid two-phase flow by weight loss measurement, electrochemical measurement and surface analysis through a loop experimental device. Besides, a quantitative analysis was performed on the pure corrosion rate, the pure erosion rate, the changed amount of corrosion rate caused by erosion, and the changed amount of erosion rate caused by corrosion and their percentages in the E-C rate, in an attempt to reveal the damage mechanism of metal materials. There were different E-C rates, electrochemical characteristics and surface morphologies at different locations of the elbow; the areas with severe E-C appeared at the bottom of the elbow and the outer part of the elbow outlet; surface morphologies were mainly presented as pits and grooves. In the total E-C rates, the percentages of pure corrosion rates and pure erosion rates were very small, while that of E-C interaction rates were large, which demonstrated that the interaction between electrochemical corrosion and mechanical erosion was the main cause of damage to metal materials. In the E-C process, mechanical erosion and electrochemical corrosion can contribute to each other, with the former playing a dominant role and the latter playing a subordinate role. |
WOS研究方向 | Electrochemistry |
语种 | 英语 |
出版者 | ESG |
WOS记录号 | WOS:000743605300008 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/154894] |
专题 | 石油化工学院 |
作者单位 | 1.Lanzhou Univ Technol, Lanzhou 730050, Peoples R China; 2.Chinese Acad Inspect & Quarantine, Lanzhou Testing Technol Co Ltd, Lanzhou 730070, Peoples R China; 3.China Univ Petr East China, Qingdao 266580, Peoples R China |
推荐引用方式 GB/T 7714 | Hu, Zongwu,Xing, Rui,Liu, Jianguo. Investigation of Erosion-corrosion of Carbon Steel Elbow in 3.5% Sodium Chloride Containing Quartz[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2022,17(1). |
APA | Hu, Zongwu,Xing, Rui,&Liu, Jianguo.(2022).Investigation of Erosion-corrosion of Carbon Steel Elbow in 3.5% Sodium Chloride Containing Quartz.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,17(1). |
MLA | Hu, Zongwu,et al."Investigation of Erosion-corrosion of Carbon Steel Elbow in 3.5% Sodium Chloride Containing Quartz".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 17.1(2022). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论