The lattice change of Ni-P layer coated on single-walled carbon nanotubes

doi:10.4028/www.scientific.net/AMR.194-196.467

CORC > 兰州理工大学 > 兰州理工大学 > 省部共建有色金属先进加工与再利用国家重点实验室

	The lattice change of Ni-P layer coated on single-walled carbon nanotubes
	Li, Wei Xue 2; Shi, Gang 1; Dai, Jian Feng 2; Wang, Qing 2
	2011
会议日期	April 9, 2011 - April 11, 2011
会议地点	Guilin, China
关键词	Intermetallics Microstructure Oxygen Before and after Electroless deposition Functionalized Intermetallic compounds Lattice expansion Lattice parameters Nanocrystalline Ni P-layer Surface modification XRD
卷号	194-196
DOI	10.4028/www.scientific.net/AMR.194-196.467
页码	467-470
英文摘要	The electroless deposition is an excellent method for the preparation of the CNTs with Ni-P layers. Pristine CNTs were first oxygen-functionalized by treating them with a mixture of concentrated (HNO3 :H 2SO4=1:3) acids. The SWNTs were obtained in the suspension of purification solution, In this work, the heat-treatment at 400°C transformed the amorphous Ni-P layer into the nanocrystalline Ni-P (crystalline Ni and Ni3P intermetallic compound) layer. The Ni-P-SWNTs before and after heat-treatment were studied using XRD and SAED. It is observed that the lattice parameters of Ni-P layers has difference from the bulk's, indicting that the lattice change has taken place. © (2011) Trans Tech Publications.
会议录	Advanced Materials Research
会议录出版者	Trans Tech Publications, P.O. Box 1254, Clausthal-Zellerfeld, D-38670, Germany
语种	英语
ISSN号	10226680
内容类型	会议论文
源URL	[http://ir.lut.edu.cn/handle/2XXMBERH/116244]
专题	省部共建有色金属先进加工与再利用国家重点实验室能源与动力工程学院
作者单位	1.School of Sciences, Lanzhou University of Technology, No.287, Langongping Road, Qilihe District, Lan Zhou, 730050, China; 2.State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, No.287, Langongping Road, Qilihe District, LanzZhou, 730050, China
推荐引用方式 GB/T 7714	Li, Wei Xue,Shi, Gang,Dai, Jian Feng,et al. The lattice change of Ni-P layer coated on single-walled carbon nanotubes[C]. 见:. Guilin, China. April 9, 2011 - April 11, 2011.