Effects of Reinforcement Volume Fraction on Mechanical Properties and Microstructures of 7075Al Matrix Composites Reinforced by FeCoCrNiAl High-Entropy Alloy Particles | |
Gao, Changqi; Wang, Qiaobo; Wei, Mingyu; Fan, Hongjing; Zhao, Libo; Wei, Yupeng; Ma, Qin | |
刊名 | METALS |
2022-05-01 | |
卷号 | 12期号:5 |
关键词 | FeCoCrNiAl high-entropy alloy reinforcements 7075Aluminium matrix composites volume fraction flexural strength and toughness failure mode |
DOI | 10.3390/met12050851 |
英文摘要 | High-entropy alloy particles reinforcements improve the mechanical properties of aluminum matrix composites while increasing its density. Investigating the effects of the reinforcement content is conducive to the fabrication of lightweight and high strength composites. FeCoCrNiAl high-entropy alloy particles (HEA(p)) reinforced 7075Al matrix composites (HEA(p)/Al) with different HEA(p) volume fractions of 5, 10, 15, and 20 vol% were fabricated via a vacuum ball milling and vacuum hot pressing sintering, and then the microstructures, interface, density, and mechanical properties of the HEA(p)/Al composites were characterized. The results indicated that composites with high relative density can be obtained with a holding time of 10 min at 580 degrees C, 30 MPa; the HEA(p) distribution was homogeneous as the increase of reinforcement volume fraction decreases and forms agglomeration, especially when the volume fraction is up to 15 vol% and 20 vol%; the density and hardness of HEA(p)/Al composites improved with the increase of reinforcements' volume fraction, whereas the flexural strength and fracture toughness of HEA(p)/Al composites increased at first and then decreased; the HEA(p)/Al composites reinforced by 10 vol% HEA(p) showed the maximum flexural strength and fracture toughness, which were increased by 124.6% and 107% compared with 7075Al, respectively; the improvement of mechanical properties was attributed to the dislocation strengthening behavior and load transfer effect of the HEA(p) reinforcement. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000804903600001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/158638] |
专题 | 材料科学与工程学院 |
作者单位 | Lanzhou Univ Technol, Sch Mat Sci & Engn, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Gao, Changqi,Wang, Qiaobo,Wei, Mingyu,et al. Effects of Reinforcement Volume Fraction on Mechanical Properties and Microstructures of 7075Al Matrix Composites Reinforced by FeCoCrNiAl High-Entropy Alloy Particles[J]. METALS,2022,12(5). |
APA | Gao, Changqi.,Wang, Qiaobo.,Wei, Mingyu.,Fan, Hongjing.,Zhao, Libo.,...&Ma, Qin.(2022).Effects of Reinforcement Volume Fraction on Mechanical Properties and Microstructures of 7075Al Matrix Composites Reinforced by FeCoCrNiAl High-Entropy Alloy Particles.METALS,12(5). |
MLA | Gao, Changqi,et al."Effects of Reinforcement Volume Fraction on Mechanical Properties and Microstructures of 7075Al Matrix Composites Reinforced by FeCoCrNiAl High-Entropy Alloy Particles".METALS 12.5(2022). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论