Quality reliability analysis of flash welding joint of cold-rolled 50JW800 silicon steel strip | |
Xu, Youwei1; Yang, Binhui1; Shi, Yu1; Feng, Xudong1; Li, Jipeng2; Feng, Changgen3; Volodymyr, Korzhyk3 | |
刊名 | Engineering Failure Analysis |
2022-08-01 | |
卷号 | 138 |
关键词 | Eddy current testing Metal cladding Recrystallization (metallurgy) Reliability analysis Silicon steel Steel sheet Strip metal Tensile testing Cold rolling (C) Eddy current testing (B) Eddy-current testing Flash welding (B) Quality reliability Quality reliability (C) Recrystallisation Silicon steel (A) Silicon steel strip Welding joints |
ISSN号 | 1350-6307 |
DOI | 10.1016/j.engfailanal.2022.106292 |
英文摘要 | In this study, the quality reliability of the flash butt welding (FBW) joint of a 50JW800 silicon steel strip is analyzed through metallographic observation, cupping tests, and tensile tests. It is found that the recrystallization in some areas of the joint is insufficient, as is the mechanically forced connection, owing to the plastic deformation and uneven heat distribution of the joint during the process of FBW. Insufficient recrystallization is the root cause of strip breakage during cold rolling. The quality reliability of the 50JW800 silicon steel strip FBW joint is also analyzed using eddy current nondestructive testing technology. It is found that the eddy current testing signal has a good response to different structural characteristics of the joint. Therefore, eddy current test technology can be used to ensure the quality reliability of silicon steel strip FBW joints in actual production. © 2022 Elsevier Ltd |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | Elsevier Ltd |
WOS记录号 | WOS:000802181700004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/158386] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Jiuquan Iron & Steel (Group) Co., Ltd, Jiayuguan; 735100, China; 3.Zhejiang E.O, Paton Welding Technology Institute, Hangzhou; 311200, China |
推荐引用方式 GB/T 7714 | Xu, Youwei,Yang, Binhui,Shi, Yu,et al. Quality reliability analysis of flash welding joint of cold-rolled 50JW800 silicon steel strip[J]. Engineering Failure Analysis,2022,138. |
APA | Xu, Youwei.,Yang, Binhui.,Shi, Yu.,Feng, Xudong.,Li, Jipeng.,...&Volodymyr, Korzhyk.(2022).Quality reliability analysis of flash welding joint of cold-rolled 50JW800 silicon steel strip.Engineering Failure Analysis,138. |
MLA | Xu, Youwei,et al."Quality reliability analysis of flash welding joint of cold-rolled 50JW800 silicon steel strip".Engineering Failure Analysis 138(2022). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论