Process Optimization and Formation Analysis of Friction Plug Welding of 6082 Aluminum Alloy | |
Zhang, Zhongke1,2; Li, Xuanbai1; Zhao, Zaolong1; Jiang, Changming1; Zhao, Huaxia3 | |
刊名 | METALS |
2020-11-01 | |
卷号 | 10期号:11 |
关键词 | friction plug welding (FPW) response surface analysis axial force flow field interaction force |
DOI | 10.3390/met10111454 |
英文摘要 | The response surface analysis method was used to systematically study the effect of various parameters on the tensile strength of 6082 aluminum alloy friction plug welding (FPW) joints in this work. The fluidity of the joint and microstructure were observed with a metallurgical microscope. Combined with the temperature field and force analysis, the reason why the root of the joint appears as a weak zone was explained. The results showed that the degree of influence on the tensile strength of FPW joints was rotational speed > upsetting speed > welding time. The optimal FPW joint was obtained when the rotational speed was 2254 rpm, the upsetting speed was 2 mm/s, and the welding time was 25 s, so the tensile strength could reach 262.34 MPa. The microstructure of the FPW joint appeared heterogeneous. According to the different plastic metal fluidities of the joint, it could be divided into four areas. The interaction force at the friction interface was not strong at the root of the FPW joint, so the root often becomes the weak area of the FPW joint. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000593178700001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/155065] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China; 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 3.AVIC Mfg Technol Inst AECC, Aeronaut Key Lab Welding & Joining Technol, Beijing 100024, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Zhongke,Li, Xuanbai,Zhao, Zaolong,et al. Process Optimization and Formation Analysis of Friction Plug Welding of 6082 Aluminum Alloy[J]. METALS,2020,10(11). |
APA | Zhang, Zhongke,Li, Xuanbai,Zhao, Zaolong,Jiang, Changming,&Zhao, Huaxia.(2020).Process Optimization and Formation Analysis of Friction Plug Welding of 6082 Aluminum Alloy.METALS,10(11). |
MLA | Zhang, Zhongke,et al."Process Optimization and Formation Analysis of Friction Plug Welding of 6082 Aluminum Alloy".METALS 10.11(2020). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论