Effect of Cold Rolling on the Microstructure and Mechanical Properties of Pure Nickel N6 | |
Jia Zhi1,2; Sun Xuan2; Ji Jinjin3; Wang Yanjiang2; Wei Baolin2; Yu Lidan2 | |
刊名 | RARE METAL MATERIALS AND ENGINEERING |
2021-10-01 | |
卷号 | 50期号:10页码:3504-3511 |
关键词 | pure nickel N6 cold rolling (CR) microstructure mechanical properties fracture behavior |
ISSN号 | 1002-185X |
英文摘要 | The effects of cold deformation on the evolution of the microstructure and mechanical properties of pure nickel N6 were investigated. Samples of pure nickel N6 were deformed by cold rolling (CR) to different thickness reductions (20%, 30%, 50%, 70%, 90%). Scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), X-ray diffraction (XRD), microhardness measurements, and tensile tests were used to characterize the microstructure and mechanical properties of the cold-rolled samples. The results show that the grains of pure nickel N6 are refined, and the grain with irregular orientation transforms into a strip-like grain with a preferred orientation parallel to the rolling direction. Micro- and nano-grains of pure nickel N6 are obtained under CR reduction of 90%, at which the grain diameter is mainly below 10 gm, accounting for 94% of the entire grain size. The distribution of low-angle grain boundaries (LAGBs) in the rolled samples is uniform, with a relatively high fraction of misorientation angles of 10 degrees from neighboring points. Upon increasing the cold rolling reductions, the tensile strength and microhardness increase, but the elongation decreases. At a CR thickness reduction of 90%, the tensile strength is 837 MPa, and the microhardness is 2479 MPa, which are 2.32 and 2.7 times higher than those in the unrolled condition, respectively. The fracture morphology of pure nickel N6 at various CR reductions include equiaxed dimples, ridges, and a step morphology, which indicate ductile fracture. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 中文 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000715969500010 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/155007] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China; 3.Lanzhou Inst Technol, Sch Mat Engn, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Jia Zhi,Sun Xuan,Ji Jinjin,et al. Effect of Cold Rolling on the Microstructure and Mechanical Properties of Pure Nickel N6[J]. RARE METAL MATERIALS AND ENGINEERING,2021,50(10):3504-3511. |
APA | Jia Zhi,Sun Xuan,Ji Jinjin,Wang Yanjiang,Wei Baolin,&Yu Lidan.(2021).Effect of Cold Rolling on the Microstructure and Mechanical Properties of Pure Nickel N6.RARE METAL MATERIALS AND ENGINEERING,50(10),3504-3511. |
MLA | Jia Zhi,et al."Effect of Cold Rolling on the Microstructure and Mechanical Properties of Pure Nickel N6".RARE METAL MATERIALS AND ENGINEERING 50.10(2021):3504-3511. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论