Formation of TiAlSi intermetallics during heating Ti-A356 Al mixed powder compact at semisolid temperature | |
Gao, M.; Chen, T.J.; Zhang, Z.X. | |
刊名 | Journal of Materials Science and Technology |
2021-12-20 | |
卷号 | 94页码:247-263 |
关键词 | Aluminum Crystal structure Morphology Oxide films Plates (structural components) Powder metals Silicon Titanium alloys Titanium oxides Anisotropic growth Combined effect Formation process In compositions Internal energies Metal materials Ternary intermetallics Tialsi intermetallics |
ISSN号 | 10050302 |
DOI | 10.1016/j.jmst.2021.04.018 |
英文摘要 | Due to the similarity in composition and crystal structure of some TiAlSi ternary intermetallics, it is quite difficult to accurately confirm their physic characteristics, and thus, to tailor microstructure to improve mechanical properties of metal materials related to the TiAlSi intermetallics. Therefore, the formation process of TiAlSi intermetallics was investigated during heating Ti-A356 mixed powder compact at a A356 alloy semisolid temperature of 595 °C. The results indicated that two kinds of intermetallics of τ1 (tetragonal, I41/amd) and τ2 (orthorhombic, Cmcm) generated, and both the concentration and supply direction of Ti atoms, which are related to local breakage of oxide films on neighboring Ti and A356 alloy powders, determined the phase and morphology of the intermetallics. τ1 and τ2 crystals all had an intrinsic plate morphology, but τ2 crystals were thinner due to more anisotropic growth resulted from their high density of stacking faults (SFs). τ1 lamellar domains generated during growth of τ2 crystals, which were accompanied by decrease in density of SFs. The combined effect of size difference and internal energy difference between τ1 and τ2 crystals made large τ1 crystals coarsen at the expense of τ2 crystals in Ostwald ripening, leading them to finally evolve into an agglomerate of large τ1 plates. © 2021 |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | Chinese Society of Metals |
WOS记录号 | WOS:000733964800004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/150730] |
专题 | 材料科学与工程学院 校医院 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Gao, M.,Chen, T.J.,Zhang, Z.X.. Formation of TiAlSi intermetallics during heating Ti-A356 Al mixed powder compact at semisolid temperature[J]. Journal of Materials Science and Technology,2021,94:247-263. |
APA | Gao, M.,Chen, T.J.,&Zhang, Z.X..(2021).Formation of TiAlSi intermetallics during heating Ti-A356 Al mixed powder compact at semisolid temperature.Journal of Materials Science and Technology,94,247-263. |
MLA | Gao, M.,et al."Formation of TiAlSi intermetallics during heating Ti-A356 Al mixed powder compact at semisolid temperature".Journal of Materials Science and Technology 94(2021):247-263. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论