Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet | |
Luo, Xiao-Mei1,3; Bi, Guang-Li1,3; Jiang, Jing1,3; Li, Ming1,3; Li, Rong-Guang2; Li, Yuan-Dong1,3; Ma, Ying1,3; Hao, Yuan1,3 | |
刊名 | Transactions of Nonferrous Metals Society of China (English Edition) |
2016-02-01 | |
卷号 | 26期号:2页码:390-397 |
关键词 | Anisotropy Compressive strength Dysprosium alloys Extrusion Microstructure Ternary alloys Textures Zinc alloys Alloy sheets Compressive strain Deformed grains Fiber texture Lpso phase Mole fraction Ultimate compressive strength Zn alloys |
ISSN号 | 10036326 |
DOI | 10.1016/S1003-6326(16)64127-4 |
英文摘要 | Compressive anisotropy of extruded Mg-2Dy-0.5Zn (mole fraction, %) alloy sheet was investigated. The alloy sheet was mainly composed of α-Mg, (Mg, Zn)xDy phase and a large number of long period stacking ordered (LPSO) phases distributed along the extrusion direction. The compressive experimental results show that the alloy sheet exhibits an obvious compressive anisotropy. The compressive strength of the specimen in the extrusion direction (ED) is higher than those of the specimens in the transverse direction (TD) and 45° inclined to the extrusion direction. The compressive yield strength (CYS), ultimate compressive strength (UCS) and compressive strain of the specimen in the ED are 274.65 MPa, 518.94 MPa and 12.93%, respectively. The compressive anisotropy is mainly attributed to the distribution of LPSO phase and formation of fiber texture in the deformed grains. © 2016 The Nonferrous Metals Society of China. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | Nonferrous Metals Society of China, B12 Fuxing Road, Beijing, 100814, China |
WOS记录号 | WOS:000369696900008 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/150222] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.School of Mechanical Engineering, Shenyang University of Chemical Technology, Shenyang; 110142, China 3.Key Laboratory of Nonferrous Metal Alloys and Processing, Ministry of Education, Lanzhou University of Technology, Lanzhou; 730050, China; |
推荐引用方式 GB/T 7714 | Luo, Xiao-Mei,Bi, Guang-Li,Jiang, Jing,et al. Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet[J]. Transactions of Nonferrous Metals Society of China (English Edition),2016,26(2):390-397. |
APA | Luo, Xiao-Mei.,Bi, Guang-Li.,Jiang, Jing.,Li, Ming.,Li, Rong-Guang.,...&Hao, Yuan.(2016).Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet.Transactions of Nonferrous Metals Society of China (English Edition),26(2),390-397. |
MLA | Luo, Xiao-Mei,et al."Compressive anisotropy of extruded Mg-Dy-Zn alloy sheet".Transactions of Nonferrous Metals Society of China (English Edition) 26.2(2016):390-397. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论