Effect of Rare Earth Elements Addition on Corrosion Behavior of Fe-based Amorphous Composites | |
Zhao Yanchun2; Li Shu2; Li Chunling1; Li Wensheng2; Kou Shengzhong2; Mao Xuejing2; Yan Fengyun2 | |
刊名 | RARE METAL MATERIALS AND ENGINEERING |
2021-07 | |
卷号 | 50期号:7页码:2592-2598 |
关键词 | amorphous alloy rare earth element microstructure corrosion resistance |
ISSN号 | 1002-185X |
英文摘要 | The Fe-15Mn-5Si-14Cr-0.2C amorphous composite rod sample added with and without rare earth elements of Ce, Dy and Ce+Dy were prepared using industrial purity raw materials treated by the coating agent (CaO-Fe2O3-SiO2). The effects of Ce, Dy and Ce+Dy rare earth elements addition on the microstructure were studied by XRD and TEM. The electrochemical workstation three-electrode system was used to test the corrosion behavior of the sample in 1 mol/L HCl and 1 mol/L NaOH. The results show that the microstructure of the alloys added with rare earth elements is amorphous composite matrix with the undercooled austenite phase CFe15.1 and the ferrite phase Fe-Cr. The corrosion resistance of the sample with 1 wt% Ce in HCl and NaOH is optimum. The self-corrosion potential in HCl is -0.16205 V, the self-corrosion current density is 7.6999 x 10(-8) A.cm(-2), and the polarization resistance reaches 9.5774x10(8) Omega.cm(2). In NaOH, the self-corrosion potential and self-corrosion current density is -0.1839 V, 1.7453x10(-8) A.cm(-2), respectively, and the polarization resistance value is 7.1574x10(8) Omega.cm(2). The corrosion resistance is obviously better than that of 304 stainless steel. It is a corrosion-resistant material with great potential. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000686209800044 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/148654] |
专题 | 材料科学与工程学院 机电工程学院 |
作者单位 | 1.Lanzhou Univ Technol, Sch Mech & Elect Engn, Lanzhou 730050, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; |
推荐引用方式 GB/T 7714 | Zhao Yanchun,Li Shu,Li Chunling,et al. Effect of Rare Earth Elements Addition on Corrosion Behavior of Fe-based Amorphous Composites[J]. RARE METAL MATERIALS AND ENGINEERING,2021,50(7):2592-2598. |
APA | Zhao Yanchun.,Li Shu.,Li Chunling.,Li Wensheng.,Kou Shengzhong.,...&Yan Fengyun.(2021).Effect of Rare Earth Elements Addition on Corrosion Behavior of Fe-based Amorphous Composites.RARE METAL MATERIALS AND ENGINEERING,50(7),2592-2598. |
MLA | Zhao Yanchun,et al."Effect of Rare Earth Elements Addition on Corrosion Behavior of Fe-based Amorphous Composites".RARE METAL MATERIALS AND ENGINEERING 50.7(2021):2592-2598. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论