Wetting of SiC by molten Cu–20Me–2Cr (Me=Ag, Mn, Si, and Sn) alloys at 1373 K | |
Lin, Qiaoli2; Liu, Lu2; Yang, Hongyu1; Li, Liumeng3 | |
刊名 | Vacuum |
2021-03-01 | |
卷号 | 185 |
关键词 | Dissolution Manganese Silicon carbide Silver Tin alloys Cr addition Critical concentration Interfacial structures Precipitation reaction Reaction layers Si addition Spreading dynamics |
ISSN号 | 0042207X |
DOI | 10.1016/j.vacuum.2020.110002 |
英文摘要 | In this work, the effect of the third addition (Ag, Mn, Si, and Sn) on the wettability and the interfacial structures of Cu–20Me–2Cr/SiC systems was investigated. The third addition Me has the obvious effect on the wettability and the spreading dynamics. The sequence of effectiveness is Sn > Ag > Mn > Si. Si Addition can suppress the precipitation of the wettable reaction products, and thus that caused the poor wettability. Although additions of Ag and Mn can improve the wettability significantly, a dissolution zone beneath the reaction layer would be formed. When the third addition Me was thermodynamically repulsive with Si. Meanwhile, the critical concentration of Si in liquid for equilibrium with SiC was less than the corresponding amount of graphite consumed by Cr addition. The dissolution zone would be suppressed. Sn addition satisfied this situation, and thus the best wettability can be achieved. The spreading of Cu–20Me–2Cr/SiC was controlled by the decomposition of SiC rather than the precipitation reaction. © 2020 Elsevier Ltd |
语种 | 英语 |
出版者 | Elsevier Ltd |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/147148] |
专题 | 材料科学与工程学院 |
作者单位 | 1.School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang; Jiangsu; 212003, China; 2.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metal, Lanzhou University of Technology, No. 287 Langongping Road, Lanzhou; 730050, China; 3.Zhejiang E.O. Paton Welding Technology Research Institute, No. 233 Yonghui Road, Hangzhou; 311200, China |
推荐引用方式 GB/T 7714 | Lin, Qiaoli,Liu, Lu,Yang, Hongyu,et al. Wetting of SiC by molten Cu–20Me–2Cr (Me=Ag, Mn, Si, and Sn) alloys at 1373 K[J]. Vacuum,2021,185. |
APA | Lin, Qiaoli,Liu, Lu,Yang, Hongyu,&Li, Liumeng.(2021).Wetting of SiC by molten Cu–20Me–2Cr (Me=Ag, Mn, Si, and Sn) alloys at 1373 K.Vacuum,185. |
MLA | Lin, Qiaoli,et al."Wetting of SiC by molten Cu–20Me–2Cr (Me=Ag, Mn, Si, and Sn) alloys at 1373 K".Vacuum 185(2021). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论