Microstructure and properties of 304L stainless steel submerged arc welding joint under different annealing conditions | |
Zhang, Jianxiao1,2; Chen, Huizi1; Feng, Wei3; Huang, Jiangkang1; Fan, Ding1 | |
刊名 | Hanjie Xuebao/Transactions of the China Welding Institution |
2019-09-25 | |
卷号 | 40期号:9页码:43-48 |
关键词 | Annealing Austenite Heat affected zone Microstructure Residual stresses Submerged arc welding Toughness Welded steel structures 304L stainless steel Annealing condition Annealing temperatures Butt joints Impact energy Impact work Microstructure and properties Microstructure of welded joints |
ISSN号 | 0253360X |
DOI | 10.12073/j.hjxb.2019400233 |
英文摘要 | The butt joint experiment of 304L stainless steel thick plate was carried out by submerged arc welding method. The microstructure and properties of 304L stainless steel welded joint were analyzed by observing the microstructure of welded joint, combining with the impact toughness of welded joint at-196 and the residual stress test under different annealing conditions. The results show that the microstructure of heat affected zone is austenite, and the weld zone is austenite + a small amount of austenite. The results show that the residual stresses in weld seam and heat affected zone change greatly after annealing, and the residual stresses are further released with the increase of annealing temperature. In impact test, the impact energy of heat-affected zone at-196 decreases sharply with the increase of annealing temperature, and the impact work in weld zone at-196 decreases sharply with the increase of annealing temperature. The impact work showed a steady downward trend. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved. |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/114638] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Lanzhou LS Heavy Equipment Co., Ltd., Lanzhou; 730314, China; 3.Harbin Well Welding Co., Ltd., Harbin; 150028, China |
推荐引用方式 GB/T 7714 | Zhang, Jianxiao,Chen, Huizi,Feng, Wei,et al. Microstructure and properties of 304L stainless steel submerged arc welding joint under different annealing conditions[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2019,40(9):43-48. |
APA | Zhang, Jianxiao,Chen, Huizi,Feng, Wei,Huang, Jiangkang,&Fan, Ding.(2019).Microstructure and properties of 304L stainless steel submerged arc welding joint under different annealing conditions.Hanjie Xuebao/Transactions of the China Welding Institution,40(9),43-48. |
MLA | Zhang, Jianxiao,et al."Microstructure and properties of 304L stainless steel submerged arc welding joint under different annealing conditions".Hanjie Xuebao/Transactions of the China Welding Institution 40.9(2019):43-48. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论