Fabrication and properties of carbon fiber reinforced Al2O3-20%Ni metal-ceramic composites | |
Wang, Min1; Jia, Jiangang1; Guo, Tieming2; Wang, Hailong2 | |
刊名 | Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica
![]() |
2017-12-01 | |
卷号 | 34期号:12页码:2778-2784 |
关键词 | Alumina Aluminum oxide Bending strength Carbon fibers Cermets Hardness Hot pressing Metal pressing Morphology Nickel Sintering Sol-gel process Sol-gels Volume fraction Carbon fiber reinforced Fracture morphology High temperature Hot pressing sintering Sintering process Strength and toughness Toughening mechanisms Well-dispersed |
ISSN号 | 10003851 |
DOI | 10.13801/j.cnki.fhclxb.20170310.001 |
英文摘要 | The CF/Al2O3-20% Ni metal-ceramic composites with 0%, 5%, 10% and 15% volume fraction of carbon fiber (CF) were prepared by sol-gel method and hot-pressing sintering. The phase composition, surface and fracture morphology were analyzed by XRD, SEM and EDS. The effect of CF content on CF/Al2O3-20%Ni hardness, bending strength, fracture toughness was studied. The fracture morphology of composites was analyzed by SEM and its mechanism was discussed. The results show that CF/Al2O3-20% Ni composites with well dispersed CF and evenly distributed Ni particles was obtained, and can prevent the loss CF in the sintering process at high temperature by the formation of α-Al2O3 protective film layer on the CF surface. With the increase of volume fraction of CF, The hardness of the CF/Al2O3-20% Ni composites reduce, and its bending strength and fracture toughness first increase and then decrease. When the CF volume fraction is 10%, the bending strength and fracture toughness reach the maximum values, which increase by 79% and 134%, respectively, compared with the composites without CF. The addition of CF improves the strength and toughness of the CF/Al2O3-20%Ni composites. The toughening mechanism of CF/Al2O3-20%Ni is CF pull out, bridge and disbonding. © 2017,Chinese Society for Composite Materials. All right reserved. |
语种 | 中文 |
出版者 | Beijing University of Aeronautics and Astronautics (BUAA) |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/114599] ![]() |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou; 730050, China; 2.School of Materials Science and Engineering, Lanzhou University and Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Wang, Min,Jia, Jiangang,Guo, Tieming,et al. Fabrication and properties of carbon fiber reinforced Al2O3-20%Ni metal-ceramic composites[J]. Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica,2017,34(12):2778-2784. |
APA | Wang, Min,Jia, Jiangang,Guo, Tieming,&Wang, Hailong.(2017).Fabrication and properties of carbon fiber reinforced Al2O3-20%Ni metal-ceramic composites.Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica,34(12),2778-2784. |
MLA | Wang, Min,et al."Fabrication and properties of carbon fiber reinforced Al2O3-20%Ni metal-ceramic composites".Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica 34.12(2017):2778-2784. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论