Effect of Er on Structure,Mechanical Properties,Thermal Stability and Amorphous Forming Ability of ZrCuNiAl Amorphous Alloy | |
Li, Chun-Yan1,2; Yin, Jin-Feng1; Wang, Zheng3; Kou, Sheng-Zhong1,2; Zhao, Yan-Chun1,2 | |
刊名 | Cailiao Gongcheng/Journal of Materials Engineering |
2018-01-20 | |
卷号 | 46期号:1页码:1-7 |
关键词 | Aluminum alloys Compressive strength Copper alloys Elastic moduli Erbium Fracture toughness Mechanical properties Plastic deformation Stability Thermodynamic stability Trace elements Zircaloy Amorphous formation Amorphous-forming ability Atom fractions Bulk amorphous alloys Compressive plastic strain Glass forming ability Zr-based amorphous alloys |
ISSN号 | 10014381 |
DOI | 10.11868/j.issn.1001-4381.2016.001421 |
英文摘要 | Focusing on (Zr0.6336Cu0.1452Ni0.1012Al0.12)100-xErx(x=0,0.5,1,1.5,2,2.5,3,atom fraction) bulk amorphous alloys, the effect of Er on the structure, mechanical properties, thermal stability and amorphous forming ability of amorphous alloys was studied by changing the content of trace element of Er. The results show that all the samples are completely amorphous alloys after the addition of Er element. With the increase of the content of Er, the elastic modulus of each sample increases firstly and then decreases, and the compressive plastic strain is stepped up, and the plastic strain of samples at x=0,x=0.5 and x=1 is fluctuating in the range of 4%; the plastic strain of samples at x=1.5,x=2,x=2.5 in the range of 11%; the plastic strain of samples at x=3 is the highest, its value is 23.19%, the elastic modulus is 37.76GPa, the yield strength is 1604MPa, the compressive strength is 2068MPa, the fracture strength is 2060MPa. With the increase of Er content, the thermal stability of Zr based amorphous alloys and amorphous formation ability decrease firstly and then increase. © 2018, Journal of Materials Engineering. All right reserved. |
WOS研究方向 | Materials Science |
语种 | 中文 |
出版者 | Beijing Institute of Aeronautical Materials (BIAM) |
WOS记录号 | WOS:000465609300001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/114458] |
专题 | 材料科学与工程学院 |
作者单位 | 1.School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 3.Sinotruk Group Jinan Truck Company Limited, Jinan; 250000, China |
推荐引用方式 GB/T 7714 | Li, Chun-Yan,Yin, Jin-Feng,Wang, Zheng,et al. Effect of Er on Structure,Mechanical Properties,Thermal Stability and Amorphous Forming Ability of ZrCuNiAl Amorphous Alloy[J]. Cailiao Gongcheng/Journal of Materials Engineering,2018,46(1):1-7. |
APA | Li, Chun-Yan,Yin, Jin-Feng,Wang, Zheng,Kou, Sheng-Zhong,&Zhao, Yan-Chun.(2018).Effect of Er on Structure,Mechanical Properties,Thermal Stability and Amorphous Forming Ability of ZrCuNiAl Amorphous Alloy.Cailiao Gongcheng/Journal of Materials Engineering,46(1),1-7. |
MLA | Li, Chun-Yan,et al."Effect of Er on Structure,Mechanical Properties,Thermal Stability and Amorphous Forming Ability of ZrCuNiAl Amorphous Alloy".Cailiao Gongcheng/Journal of Materials Engineering 46.1(2018):1-7. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论