Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel | |
Yang, Guirong2; Gao, Dawen2; Song, Wenming1; Zhang, Yufu1; Ma, Ying2 | |
刊名 | Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research
![]() |
2019-02-25 | |
卷号 | 33期号:2页码:87-94 |
关键词 | Cladding (coating) Composite coatings Composite materials Diffusion Melting point Nickel alloys Nickel coatings Sintered carbides Steel metallurgy Ternary alloys Diffusion-affected zone Formation mechanism Heat preservation Nickel-based composites Phase constituent Thick composites Transition layers Uniform distribution |
ISSN号 | 10053093 |
DOI | 10.11901/1005.3093.2018.510 |
英文摘要 | Ni+WC composite cladding was prepared on the surface of 45 # steel by vacuum cladding technology. The formation mechanism of nickel-based composite coating was investigated by intermittently sampling. The results show that a Ni-based composite cladding with metallurgical fusion to the matrix and uniform distribution of WC hard particles is obtained on the surface of 45 steel. The entire cladding consists of a 4 mm thick composite layer, a 1 mm thick transition layer, a 20 μm thick diffusion fused zone, and a 250 μm thick diffusion affected zone. The composite layer composes of WC and W-rich multiphase carbide formed after decomposition, surrounded by Ni particles; The main phase constituents of the composite cladding layer include γ- Ni solid solution, Cr7C3, Ni2.9Cr0.7Fe0.36, Cr23C6, Ni3Fe, Ni3Si, Ni3B, W2C and C. The vacuum cladding process mainly includes the formation of a micro-sintered neck between the particles in the heating stage before the Ni-based alloy particles reach its melting point, and the melting of the Ni-based alloy particles at the beginning stage of its melting point and the third stages of fusion diffusion in the heat preservation stage and position adjustment of the WC particle within micro-area. © All right reserved. |
语种 | 中文 |
出版者 | Chinese Journal of Materials Research |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/114105] ![]() |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanpec Technologies Co. Ltd., Lanzhou; 730070, China 2.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; |
推荐引用方式 GB/T 7714 | Yang, Guirong,Gao, Dawen,Song, Wenming,et al. Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel[J]. Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,2019,33(2):87-94. |
APA | Yang, Guirong,Gao, Dawen,Song, Wenming,Zhang, Yufu,&Ma, Ying.(2019).Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel.Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,33(2),87-94. |
MLA | Yang, Guirong,et al."Formation Mechanism of Ni/WC Composite Coatings on Carbon Steel".Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research 33.2(2019):87-94. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论