Relationship between thermal process and microstructure during additive manufacturing of double-electrode gas metal arc welding | |
Yu, Shurong1,2; Cheng, Nengdi1; Huang, Jiankang2; Yu, Xiaoquan2; Fan, Ding2 | |
刊名 | Hanjie Xuebao/Transactions of the China Welding Institution |
2019-08-25 | |
卷号 | 40期号:8页码:1-6 |
关键词 | 3D printers Additives Dendrites (metallography) Gas welding Microhardness Microstructure Plasma welding Welding electrodes Additive manufacture Dendrite arm spacing Micro-plasma arc welding Micro-plasmas Microstructure and properties Microstructure observation Thermal cycle curve Thermal process |
ISSN号 | 0253360X |
DOI | 10.12073/j.hjxb.2019400200 |
英文摘要 | Wire arc additive manufacture of ER304L stainless steel was studied using double electrode micro-plasma arc welding. The effect of different bypass current and stacking sequence on the microstructure and properties of 304 stainless steel stacking samples were analyzed by microstructure observation and microhardness test. Combining with the thermal cycle curve measured in the process of additive manufacturing. The results show that when the bypass current is increased, the dendrite arm spacing of the stacking sample decreased firstly and then increased during additive manufacturing of double electrode micro-plasma arc welding. Meanwhile, the effect of stacking sequence on microstructure was that the different direction of heat dissipation leaded to the change of dendrite growth direction. The microhardness decreased slowly along the direction of stack height. And with the increase of the bypass current, the hardness increases firstly and then decreases. The stacking order had no obvious effect on the hardness. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved. |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/113828] |
专题 | 材料科学与工程学院 |
作者单位 | 1.School of Mechanical and Electrical Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.State Key Laboratory of advanced processing and recycling of Non-Ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Yu, Shurong,Cheng, Nengdi,Huang, Jiankang,et al. Relationship between thermal process and microstructure during additive manufacturing of double-electrode gas metal arc welding[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2019,40(8):1-6. |
APA | Yu, Shurong,Cheng, Nengdi,Huang, Jiankang,Yu, Xiaoquan,&Fan, Ding.(2019).Relationship between thermal process and microstructure during additive manufacturing of double-electrode gas metal arc welding.Hanjie Xuebao/Transactions of the China Welding Institution,40(8),1-6. |
MLA | Yu, Shurong,et al."Relationship between thermal process and microstructure during additive manufacturing of double-electrode gas metal arc welding".Hanjie Xuebao/Transactions of the China Welding Institution 40.8(2019):1-6. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论