Microstructure and mechanical property of welding-brazing joint between aluminum and steel by micro-beam plasma welding | |
Fan, Ding1,2; Kang, Yutao2; Huang, Jiankang1; Yu, Xiaoquan2; Pan, Wei2 | |
刊名 | Hanjie Xuebao/Transactions of the China Welding Institution
![]() |
2019-02-25 | |
卷号 | 40期号:2页码:20-25 |
关键词 | Beam plasma interactions Binary alloys Brazing Galvanizing Intermetallics Iron alloys Materials testing apparatus Metal testing Microstructure Morphology Plasma welding Scanning electron microscopy Slags Spectrometers Tensile strength Tensile testing Welding Welds Energy dispersive spectrometers Intermetallic compound layer Joint strength Metallographic microscope Micro beams Microstructure and mechanical properties Spreading width Tensile testing machines |
ISSN号 | 0253360X |
DOI | 10.12073/j.hjxb.2019400035 |
英文摘要 | Butt welding-brazing joint between 6010 aluminum alloy and galvanized steel sheets was obtained by micro-beam plasma welding method. A sound weld joint could be obtained in the suitable welding parameter. The analysis was carried out for the weld joint morphology, microstructure and mechanical property using metallographic microscope, scanning electron microscope, energy-dispersive spectrometer and universal tensile testing machine. The results show that a good spreading width is got in back and front sides of weld joint, there are no obvious crack, pore, slag in the joint, and the joint shows a typical welding-brazing characteristic. The serrated intermetallic compound Fe2Al5 is formed at the interface. The joint strength is determined by the thickness of intermetallic compound layer and the spreading width. When the welding current is 38.5 A, the tensile strength of weld joint is 193 MPa, which can reach 79.8% of aluminum base material. The fracture form of joint is ductile-brittle fracture. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved. |
语种 | 中文 |
出版者 | Harbin Research Institute of Welding |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/113825] ![]() |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Fan, Ding,Kang, Yutao,Huang, Jiankang,et al. Microstructure and mechanical property of welding-brazing joint between aluminum and steel by micro-beam plasma welding[J]. Hanjie Xuebao/Transactions of the China Welding Institution,2019,40(2):20-25. |
APA | Fan, Ding,Kang, Yutao,Huang, Jiankang,Yu, Xiaoquan,&Pan, Wei.(2019).Microstructure and mechanical property of welding-brazing joint between aluminum and steel by micro-beam plasma welding.Hanjie Xuebao/Transactions of the China Welding Institution,40(2),20-25. |
MLA | Fan, Ding,et al."Microstructure and mechanical property of welding-brazing joint between aluminum and steel by micro-beam plasma welding".Hanjie Xuebao/Transactions of the China Welding Institution 40.2(2019):20-25. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论