Reactive wetting of low carbon steel by Al 4043 and 6061 alloys at 600-750 °C | |
Lin, Qiaoli; Jin, Peng; Cao, Rui; Chen, Jianhong | |
刊名 | Surface and Coatings Technology
![]() |
2016-09-25 | |
卷号 | 302页码:166-172 |
关键词 | Activation energy Capillarity Coatings Low carbon steel Magnesium alloys Oxide films Silicon alloys Wetting Apparent activation energy Chemical compositions Infiltration mechanisms Interfacial structures Modified sessile drop method Oxidized surfaces Reduction reaction Spreading dynamics |
ISSN号 | 02578972 |
DOI | 10.1016/j.surfcoat.2016.06.005 |
英文摘要 | Wetting of low carbon steel by two industrial grades Al (4063 and 6061) alloys was investigated by the modified sessile drop method at temperatures between 600 and 750 °C under high vacuum. The formation of intermetallics which would lead to the replacement of the oxidized surface by a clean surface, and further induces the spreading. The formation of precursor film in the wetting of Al 6061/steel was caused by subcutaneous infiltration mechanism. The different chemical compositions in Al alloys also lead to the different interfacial structures and spreading dynamics. The Mg in Al 6061 alloy reduces the oxide film and then make molten Al is easier to infiltrate into the steel substrate; the high affinity of the Si in Al 4043 alloy at Al/steel interface which induced the segregation of Si. The reduction reaction by the Mg in Al 6061 and the reaction between Al and Fe caused the apparent activation energy for spreading is almost an order of magnitude larger than Al 4043. © 2016 Elsevier B.V.. |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
出版者 | Elsevier B.V. |
WOS记录号 | WOS:000381838400020 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/112594] ![]() |
专题 | 材料科学与工程学院 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metal, Lanzhou University of Technology, No.287 Langongping Road, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Lin, Qiaoli,Jin, Peng,Cao, Rui,et al. Reactive wetting of low carbon steel by Al 4043 and 6061 alloys at 600-750 °C[J]. Surface and Coatings Technology,2016,302:166-172. |
APA | Lin, Qiaoli,Jin, Peng,Cao, Rui,&Chen, Jianhong.(2016).Reactive wetting of low carbon steel by Al 4043 and 6061 alloys at 600-750 °C.Surface and Coatings Technology,302,166-172. |
MLA | Lin, Qiaoli,et al."Reactive wetting of low carbon steel by Al 4043 and 6061 alloys at 600-750 °C".Surface and Coatings Technology 302(2016):166-172. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论