Fracture behaviour of 8%Ni 980 MPa high strength steel at various temperatures Part 2 - COD tests | |
Cao, R.1,2; Yan, Y. J.1,2; Du, W. S.3; Tian, Z. L.3; Peng, Y.3; Chen, J. H.1,2 | |
刊名 | Materials Science and Technology
![]() |
2011 | |
卷号 | 27期号:1页码:145-155 |
关键词 | Bainite Cracks Fracture Fracture mechanics Grain boundaries Steel testing Temperature Austenite grain boundaries Crack configuration Crack opening displacements Effects of temperature Fracture behaviour Fracture mechanisms Microscopic observations of fracture Very low temperatures |
ISSN号 | 02670836 |
DOI | 10.1179/174328409X439169 |
英文摘要 | The fracture behaviour of 8%Ni 980 MPa grade high strength steel is investigated by combining experimental results of crack opening displacement (COD) tests at various temperatures with detailed microscopic observations of fracture surfaces and crack configurations in unloaded specimens. The results reveal that this high strength steel possesses high toughness with a transition temperature around -150°C. Even though at a very low temperature (-196°C), cleavage cracking dominates the fracture process and the crack does not propagate immediately through the entire ligament: a 'pop-in' extension is observed in macroscopic tests, and the microscopic fracture mode is quasi-cleavage. It is found that resistance to crack propagation is provided by three barriers: original austenite grain boundaries, bainite colony boundaries and interlayers between bainite laths. These barriers manifest themselves by tear ridges with dimples on the fracture surfaces. At higher temperatures, the fracture mechanism is dominated by fibrous rupture, associated with a 'dimpled' fracture surface and some individual quasi-cleavage facets. © 2011 Institute of Materials, Minerals and Mining Published by Maney on behalf of the Institute. |
资助项目 | Foundation for Doctorate of Education Ministry[20060731001] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | Maney Publishing |
WOS记录号 | WOS:000285870400026 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/111561] ![]() |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 材料科学与工程学院 |
通讯作者 | Cao, R. |
作者单位 | 1.Lanzhou Univ Technol, Minist Educ, Key Lab Nonferrous Met Alloys, Lanzhou 730050, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Gansu Adv Nonferrous Met Mat, Lanzhou 730050, Peoples R China 3.Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China |
推荐引用方式 GB/T 7714 | Cao, R.,Yan, Y. J.,Du, W. S.,et al. Fracture behaviour of 8%Ni 980 MPa high strength steel at various temperatures Part 2 - COD tests[J]. Materials Science and Technology,2011,27(1):145-155. |
APA | Cao, R.,Yan, Y. J.,Du, W. S.,Tian, Z. L.,Peng, Y.,&Chen, J. H..(2011).Fracture behaviour of 8%Ni 980 MPa high strength steel at various temperatures Part 2 - COD tests.Materials Science and Technology,27(1),145-155. |
MLA | Cao, R.,et al."Fracture behaviour of 8%Ni 980 MPa high strength steel at various temperatures Part 2 - COD tests".Materials Science and Technology 27.1(2011):145-155. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论