Effects of annealing treatment on microstructure and electrochemical properties of La0.68Gd0.2Mg0.12 Ni3.3Co0.3Al0.1 hydrogen storage alloys | |
Fang, Xiao-Fei1; Luo, Yong-Chun1,2; Gao, Zhi-Jie1; Zhang, Guo-Qing1; Kang, Long1,2 | |
刊名 | Gongneng Cailiao/Journal of Functional Materials |
2012-10-30 | |
卷号 | 43期号:20页码:2751-2756 |
关键词 | Aluminum
Cerium
Cerium alloys
Electrochemical properties
Gadolinium
Hydrogen storage alloys
Inductively coupled plasma
Lanthanum
Lithium compounds
Microstructure
X ray diffraction
A |
ISSN号 | 10019731 |
英文摘要 | La0.68Gd0.2Mg0.12 Ni3.3Co0.3Al0.1 hydrogen storage alloys were prepared by induction melting and then annealed at different temperature(1173-1273K) in the closed container for 16h. The effect of annealing temperature on the microstructure and electrochemical properties of La0.68Gd0.2Mg0.12 Ni3.3Co0.3Al0.1 were investigated by means of inductively coupled plasma(ICP), X-ray diffraction (XRD), electron probe micro-analysis (EPMA) and electrochemical measurements. The results showed that the A5B19 alloys mainly consisted of Ce5Co19-type (Pr5Co19-type), PuNi3-type and CaCu5-type phase. Meanwhile, with increasing annealing temperature, Pr5Co19-type phase abundance in annealed alloys increased, and Ce5Co19-type phase abundance decreased. The Pr5Co19-type phase abundance was 87.75wt%, and Ce5Co19-type phase abundance was only 0.78wt% when annealing temperature was 1273K. The electrochemical measurements showed that these alloys had little effects on activation performance under different annealing temperature, but it was great impact on electrode capacity and cycle stability. The discharge capacity of the alloys reached 373.01mAh/g when annealing temperature was 1273K. After 100 charge-discharge cycles, the discharge capacity retention rate(S100) of the alloy electrode(T=1273K) reached 90.2%. |
语种 | 中文 |
出版者 | Journal of Functional Materials, P.O. Box 1512, Chongqing, 630700, China |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/110989] |
专题 | 材料科学与工程学院 |
作者单位 | 1.College of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China; 2.State Key Laboratory of Gansu Advanced Non-Ferrous Materials, Lanzhou University of Technology, Lanzhou 730050, China |
推荐引用方式 GB/T 7714 | Fang, Xiao-Fei,Luo, Yong-Chun,Gao, Zhi-Jie,et al. Effects of annealing treatment on microstructure and electrochemical properties of La0.68Gd0.2Mg0.12 Ni3.3Co0.3Al0.1 hydrogen storage alloys[J]. Gongneng Cailiao/Journal of Functional Materials,2012,43(20):2751-2756. |
APA | Fang, Xiao-Fei,Luo, Yong-Chun,Gao, Zhi-Jie,Zhang, Guo-Qing,&Kang, Long.(2012).Effects of annealing treatment on microstructure and electrochemical properties of La0.68Gd0.2Mg0.12 Ni3.3Co0.3Al0.1 hydrogen storage alloys.Gongneng Cailiao/Journal of Functional Materials,43(20),2751-2756. |
MLA | Fang, Xiao-Fei,et al."Effects of annealing treatment on microstructure and electrochemical properties of La0.68Gd0.2Mg0.12 Ni3.3Co0.3Al0.1 hydrogen storage alloys".Gongneng Cailiao/Journal of Functional Materials 43.20(2012):2751-2756. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论